The dependence of the mechanism of age hardening in Al-Mg-Si alloys on their Si content, the pre-aging conditions and addition of Cu has been investigated. For this purpose, the solute clusters and the metastable precipitates in aged Al-Mg-Si alloys have been characterized by a three dimensional atom probe (3DAP) and transmission electron microscopy (TEM). Atom probe analysis results have revea...

The age-hardening behavior of Fe−25.3Ni−1.7 Ti (wt pct) alloy both in undeformed specimens and in specimens cold deformed by 10 or 20 pct prior to aging was studied. The microstructural changes during aging were observed using transmission electron microscopy (TEM) and atom probe analysis and there were related to the mechanical properties as measured by microhardness and shear punch testing. A...

The addition of cobalt was experimentally observed to increase the strength and impact toughness of Cu precipitation hardened steel. In order to understand the mechanism of this strengthening, we studied the effect of cobalt in the bulks and surfaces of bcc Fe and bcc Cu, as well as at the Fe/Cu interface by ab initio density-functional approach. We investigated the cobalt distribution between ...

2024 Aluminum alloy was squeezed cast by the Gas Induced Semi Solid (GISS) process. Effect of artificial aging on microstructure and mechanical properties of this alloy was studied in the present work. The solutionized specimens were aged hardened at temperatures of 175°C, 200°C, and 225°C under various time durations. The highest hardness of about 77.7 HRE was attained from specimen aged at th...

The mechanical properties of GH4169 alloy sheet after cold rolling (at 0%, 10%, 30%, 50% and 70%) and solid solution were investigated. The textures and Taylor factors were characterized using electron backscattering diffraction (EBSD). The fractions of δ phase were measured by X-ray diffraction. The contributions of δ phase, grain size, texture, and work hardening on the mechanical properties ...