In this study, effect of immersion time on the electrochemical behaviour of AISI 321 stainless steel (AISI 321) in 0.1 M H 2SO 4 solution under open circuit potential (OCP) conditions was evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Mott–Schottky analysis revealed that the passive films behave as n-type and p-type s...

The corrosion inhibitive action of flower extracts of Clitoria ternata flower on mild steel corrosion in 0.5 M H2SO4 solution was studied using weight loss method, potentiodynamic polarization and EIS measurements. The results obtained indicate that the extracts functioned as good inhibitors in 0.5 M H2SO4 solution. Inhibition efficiency was found to increase with extract concentration. The ads...

A practical anodic and cathodic curve intersection model, which consisted of an apparent anodic curve and an imaginary cathodic line, was proposed to explain multiple corrosion potentials occurred in potentiodynamic polarization curves of Fe-based glassy alloys in alkaline solution. The apparent anodic curve was selected from the measured anodic curves. The imaginary cathodic line was obtained ...

Electrochemical synthesis of poly ortho toludine (POTD) was achieved on Teflon coated cylindrical stainless steel electrodes with base diameter 2mm . Aniline in 2-propyl pentatonic acid solution was polymerized on the surface of stainless steel using cyclic voltametry technique. Adherent and red polymer films were obtained on the electrodes.. The corrosion inhibitive performance of POTD+2PPA , ...

this paper focused on the characterization of electrochemical behavior of a martensitic stainless steel inthe acidic solutions. for this purpose, electrochemical parameters were derived from potentiodynamicpolarization, mott schottky analysis and electrochemical impedance spectroscopy (eis) techniques.the potentiodynamic polarization results showed that corrosion current density of aisi 420 sta...

in this study, the effects of forming method (extrusion) and environmental factors (solution ph and temperature) on the corrosion performance of az91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (eis), scanning electron microscopy (sem) and salt spray techniques. the polarization test results of the specimens showed that simple sh...

y-tial intermetallic alloy have a good potential for use as biomaterial, due to its good corrosion resistance. in this paper, two fundamental electrochemical techniques namely electrochemical impedance spectroscopy and potentiodynamic anodic polarization were used to evaluate the corrosion performance of g-tial in ringer's solution. surface modification treatments were employed with the pu...

The corrosion inhibitive action of oxystelma esculentum stem on mild steel corrosion in 0.5 M H2SO4 solution was studied using weight loss method, potentiodynamic polarization and EIS measurements. The results obtained indicate that the extracts functioned as good inhibitors in 0.5 M H2SO4 solution. Inhibition efficiency was found to increase with extract concentration. The adsorption of consti...

Ion implantation is a surface modification technology to produce new material on the surface by impingement of high energy ions from the ion accelerator. In this work, AISI 304 stainless steels were coated with 90 nm Ni film by electron beam deposition and implanted by a flow of 5×1017 N cm−2 at 400 K temperature with different implantation energies of 10, 20, 30 and 40 keV. The prepared sample...

The purpose of this study is to understand the electrochemical corrosion behavior of 1wt% Cu content Al-6Si-0.5Mg alloy in 0.1M NaCl solution. The potentiodynamic polarization curves reveal that 1wt% Cu content alloy is less prone to corrosion than the Cu free alloy. The EIS test results show that corrosion resistance or polarization resistance (Rct) increases with the addition of 1wt% Cu to Al...