Silica sol nano-abrasives with large particle are prepared and characterized by TEM, PCS and Zeta potential in this paper. Results show that the silica sol nano-abrasives about 100nm are of higher stability (Zeta potential: -65mV) and narrow distribution of particle size. And then alkali CMP slurries for tungsten containing self-made silica sol nanoabrasives are prepared and applied. CMP result...

In this study, different contents of Nano-silica, 2 wt.%, 4 wt.% and 6 wt.%, have been added to bitumen to modify the physical, mechanical and rheological properties of warm mix asphalt (WMA). WMA is containing 2 wt.% of Sasobit (mixture of long-chain hydrocarbons). Various quality control tests have been carried out to characterize the modified bitumen and WMA. The rheo...

Spontaneous movement of condensed matter provides a new insight to efficiently improve condensation heat transfer on superhydrophobic surface. However, very few reports have shown the jumping behaviors on the sprayable superhydrophobic coatings. Here, we developed a sprayable silica nano-porous coating assembled by fluorinated nano-chains to survey the condensates' dynamics. The dewdrops were c...

Phosphoglyceride phosphorus is readily determined directly on silica gel removed from thin-layer chromatograms, without elution, by a nondigestive procedure with a sulfuric-periodic acid reagent. The method is specific for hydrolyzable phosphoglyceride containing two acid-hydrolyzable groups. Cariolipin reacts only partially, while sphingomyelin, diether lecithin, and phosphonate cephalin fail ...

A novel method of preparing the macrporous nickel coating was described. The macrporous nickel coating was fabricated by employing nano-silica as the template. The effects of technological conditions and the concentration of the additives on the surface quality of coating were investigated, the nano-silica was characterized transmission electron microscopy (TEM) and laser particle size analyzer...

Phosphoglyceride phosphorus is readily determined directly on silica gel removed from thin-layer chromatograms, without elution, by a nondigestive procedure with a sulfuric-periodic acid reagent. The method is specific for hydrolyzable phosphoglyceride containing two acid-hydrolyzable groups. Cariolipin reacts only partially, while sphingomyelin, diether lecithin, and phosphonate cephalin fail ...

The sol-gel technique was used to prepare epoxy/silica nano-hybrids. The thermal characteristics, curing kinetics and structure of epoxy/silica nano-hybrids were studied using differential scanning calorimetry (DSC), 29Si nuclear magnetic resonance (NMR) and transmission electron microscopy (TEM). To improve the compatibility between the organic and inorganic phases, a coupling agent was used t...

Products for thin layer chromatography Ready-to-use layers for TLC Summary of MN ready-to-use layers for TLC 263 – 265 TLC ready-to-use layers with standard silica 266 – 269 TLC ready-to-use layers with concentrating zone 269 HPTLC ready-to-use layers with nano silica 269 – 271 Nano plates with extremely thin silica layer 271 TLC and HPTLC plates with modified silica layers 272 – 277 HPTLC read...

Using nano-technology materials in the asphalt pavement industry is new compared with Portland cement concrete. The main objective of this study is to investigate the effects of nano-silica modification on some properties of a penetration grade asphalt cement and a typical asphalt concrete. 60/70 penetration grade bitumen was modified with different percentages of nano-silica (i.e. 1, 3 and 5%,...

Nano-silica-bonded 3-n-propyl-1-sulfonic acid imidazolium chloride (nano-SB-[PSIM]Cl) was applied as a highly efficient, general and heterogeneous catalyst for one pot multi-component reaction of 2-naphthol, arylaldehydes, and thioacetamide leading to 1-thioamidolakyl-2-naphthols. All reactions proceeded with excellent yields in short times under solvent-free conditions. Our protocol was superi...