Atomic layer deposition (ALD) has been employed to modify the surface of high voltage cathode LiNi0.5Mn1.5O4 by coating ultrathin Al2O3 layer on the electrodes. The ultrathin layer of Al2O3 can suppress the undesirable reactions during cycling, while maintaining the electron and ion conductivity of the electrode. The ALD Al2O3 coated LiNi0.5Mn1.5O4 showed remarkable improvement over bare LiNi0....

Erbium-doped GaN (GaN:Er) epilayers were synthesized by metal organic chemical vapor deposition. GaN:Er waveguides were fabricated based on four different GaN:Er layer structures: GaN:Er/GaN/Al2O3, GaN:Er/GaN/AlN/Al2O3, GaN:Er/GaN/Al(0.75)Ga(0.25)N/AlN/Al2O3, and GaN/GaN:Er/GaN/Al2O3. Optical loss at 1.54 μm in these waveguide structures has been measured. It was found that the optical attenuat...

The oxidative dehydrogenation (ODH) of propane was investigated on vanadia dispersed on alumina containing a nominal polymolybdate monolayer (4.8 Mo/nm2). Dehydrogenation rates and selectivities on these catalysts were compared with those on vanadia domains dispersed on alumina. At a given vanadia surface density, ODH reaction rates per gram of catalyst were about 1.5–2 times greater on MoOx -c...

The short lifetime of photogenerated charge carriers of hematite (α-Fe2O3) thin films strongly hindered the PEC performances. Herein, α-Fe2O3 thin films with surface nanowire were synthesized by electrodeposition and post annealing method for photoelectrocatalytic (PEC) water splitting. The thickness of the α-Fe2O3 films can be precisely controlled by adjusting the duration of the electrodeposi...

ALD Al2O3/GaAs and Al2O3/In0.2Ga0.8As MOS and source-drain implanted MOSFET structure were fabricated and characterized by capacitance-voltage (CV) and current-voltage (I-V) measurements. It is shown that, after high-temperature anneal, the MOS leakage current density of the thinner (16nm) film is much higher than that of the thicker (30nm) film. The highquality Al2O3 (30nm)/In0.2Ga0.8As interf...

We report on the suitability of water-soluble non-polymeric electrospun cyclodextrin (CD) nanofiber templates by using atomic layer deposition (ALD) to yield metal oxide tubes. To demonstrate this, watersoluble electrospun CD nanofibers were chosen as template to produce metal oxide tubes where we have tested two examples of ALD coatings, namely, Al2O3 and ZnO. After the ALD coating on the CD n...

The interactions between 1-butyl-3-methylimidazolium trifluoromethanesulfonate ([BMIM][TFS]) and nano-Al2O3 are studied using high-pressure infrared spectroscopy. The thickness of the [BMIM][TFS] interfacial layer on the aluminum oxide are adjusted by controlling the number of washes with ethanol. In contrast to the results obtained under ambient pressure, local structures of both the cations a...

This paper describes the results of room temperature joining of TiO2 / SiO2 IRF by sputter deposition with a special emphasis of improvement of adherence at the interface. This multilayer system is designed to shield the infrared energy of solar spectrum by interference reflection. The abrasion resistance of the multilayer stacks was also estimated by the Haze value after the Taber abrasion tes...

Nanostructured ceramics and their composites possess improved properties such as tensile strength, fatigue strength, hardness, and wear resistance. Freestanding, near-net shape, nanostructured Al2O3 components can be synthesized via plasma-spray forming. In this study, plasma-spray parameters were optimized and an innovative substrate cooling technique was developed to retain nanosize Al2O3 in ...

The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over alumina supported nickel catalysts prepared by impregnation reduction method and mechanical mixing method. The catalysts were characterized by XRD and FESEM. The results show that the nickel particle diameter of alumina supported nickel prepared by impregnation reduction method (denoted as Ni/Al2O3) is slightly ...