Abstract The welding heat-affected zone (HAZ) of C-HRA-2 nickel-based alloy at different peak temperatures (T p ) (850 to 1450 °C) was obtained through thermal simulation. microstructure the simulated HAZs characterized by an optical microscope (OM), a scanning electron (SEM), and transmission (TEM). microhardness examined using tester. results indicated that fine dispersed M 23 C 6 carbides we...

High temperature tensile tests have been conducted on samples of a Fe-Ni based superalloy, Incoloy A-286, and significant ductility loss has been observed at 1220 °C. Titanium-rich, thin-film-like phase has been found on the inter-granular facets of fracture surfaces. It appears that sulfur content of Ti-rich phase was higher than that of the matrix. At 1220 °C, liquation of Ti-rich phases has ...

Variant Stochastic cracking is a significantly more resilient approach to adaptive indexing. It showed [1]that Stochastic cracking uses each query as a hint on how to reorganize data, but not blindly so; it gains resilience and avoids performance bottlenecks by deliberately applying certain arbitrary choices in its decision making. Therefore bring, adaptive indexing forward to a mature formulat...

_____________________________________________________________ Different catalysts based on Y-zeolite, ZSM-5 and amorphous kaolin were prepared and characterized. The catalytic cracking of 1,3,5-triisopropylbenzene (1,3,5-TIPB), 1,4diisopropylbenzene (1,4-DIPB) and n-dodecane were used to investigate the effect of catalyst nature on the catalytic performance. Cracking the largest molecule (1,3,5...

The varestraint cracking test was carried out to assess the hot cracking tendency of alloy 800 at different welding conditions and augmented strain levels. The test results revealed that the hot cracking susceptibility of alloy 800 increases with increasing the heat input and augmented strain levels. This emphasizes the role of constraint either internally induced or externally applied to the w...

In support of the initiatives for implementing the new MechanisticEmpirical Pavement Design Guide (MEPDG) in Iowa, a preliminary sensitivity study was undertaken to assess the comparative effect of design input parameters pertaining to material properties, traffic and climate on performance of two existing flexible pavements in Iowa with relatively thick Asphalt Concrete (AC) layers. A total of...

because thin plate reinforced concrete members such as walls and slabs are greatly influenced by the drying shrinkage, cracks can occur in these members due to the restraint of the volume change caused by drying shrinkage. therefore, the control of cracking due to drying shrinkage is very important in building construction that the thin plate members are frequently used. however, few researches...

Cline, J. A. and Trought, M. 2007. Effect of gibberellic acid on fruit cracking and quality of Bing and Sam sweet cherries. Can. J. Plant Sci. 87: 545–550. Rain-induced cracking of sweet cherries (Prunus avium L.) is a major problem in many cherry growing regions throughout the world. One method to reduce cracking is to grow cracking resistant cultivars; however, no completely effective control...

In the purely theoretical approach of pavement design, percentage fatigue cracking is related to damage in a probabilistic manner according to the Miner’s law. Two methods that are currently widely in use are based on assumptions of damage distribution. One method assumes fatigue damage being normally distributed, while the other one assumes fatigue damage being lognormally distributed. Since m...