The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...

Rationale Stable isotope analysis of leaf material has many applications including assessment plant water-use efficiency and palaeoclimatology. To facilitate interpretations small shifts in the carbon composition (δ13C) leaves, accurate repeatable results are required. Pre-sample homogenisation is essential to ensure a representative sample analysed, but can also introduce error. Methods We inv...

The morphological and microstructural changes during mechanical milling of Al powder mixed with 2.5, 5 and 10 wt.% Al2O3 particles were studied. The milling was performed in a planetary ball mill for various times up to 20 h. The produced composite powders were investigated using X-ray diffraction pattern (XRD) to elucidate the role of particle size, secondary phase content and milling time on ...

Mechanical alloying of binary and ternary elemental powder mixtures with the nominal compositions of Mg2Ni and Mg(2-x)MnxNi (x= 0, 0.05, 0.10 and 0.15 at. %) were carried out in a planetary ball mill for various milling times of 5, 10, 15, 20, 30 and 60 h. X-ray diffraction and field emission scanning and transmission electron microscopy were used for the characterization of the milled products...

Production of nanostructured aluminum matrix composite powder by high energy ball milling is investigated. Scanning electron microscopy analysis as well as the tap and green density measurements were used to optimize the milling time needed for the completion of the mechanical milling process. Also, we studied the particles morphology and size distribution change with milling time and its corre...

The room-temperature magnetic properties of ball-milled strontium hexaferrite particles consolidated by spark-plasma sintering are strongly influenced by the milling time. Scanning electron microscopy revealed the ball-milled SrFe12O19 particles to have sizes varying over several hundred nanometers. X-Ray powder-diffraction studies performed on the ball-milled particles before sintering clearly...

Benzoic acid and o-phenylenediamine efficiently reacted under the green solvent-free Ball Milling method. Several reaction parameters were investigated such as rotation frequency; milling balls weight and milling time. The optimum reaction condition was milling with 56.6 g weight of balls at 20 Hz frequency for one hour milling time. The study was extended for synthesis of a series of benzimida...

In this study, we describe the growth of carbon nanotubes on commercial iron nanoparticles without carbon shell (Fe (nm), size 2O3 and Fe* (nm)/MgO) was carried out by mixing commercial Fe* nanoparticles (as catalyst) with Al2O3 and MgO powders (as supports)by using ball-milling method. The results show in spite of the fact that ball-milling process can have neg...

Mechanochemistry continues to reveal new possibilities in chemistry including the opportunity for “greening” reactions. Nevertheless, a clear understanding of the energetic transformations within mechanochemical systems remains elusive. We employed a uniquely modified ball mill and strategically chosen Diels–Alder reactions to evaluate the role of several ball-milling variables. This revealed t...