Metal-on-metal (M-M) joint replacement has raised concerns about the long-term effects of metal wear debris and corrosion products. This review summarizes the current concepts in biological reactivity to metal wear particles, ions, and corrosion products. Attention is focused on Co-Cr-Mo alloy since it is the most diffused and discussed material in arthroplasty.

Hundreds of tons of depleted uranium (DU) ammunition were used in previous armed conflicts in Iraq, Bosnia and Herzegovina, and Serbia/Kosovo. The majority (>90%) of DU penetrators miss their target and, if left in the environment, corrode in these postconflict zones. Thus, the best way to understand the fate of bulk DU material in the environment is to characterize the corrosion products of in...

The purpose of this study was to investigate the effects of 316L stainless steel (SS) corrosion products on the in vitro biomineralization process, because tissue necrosis, bone loss, impaired bone mineralization, and loosening of orthopedic implants are associated with ions and debris resulting from biodegradation. Rat bone marrow cells were cultured in experimental conditions that favored the...

The effect of oil soluble commercial corrosion inhibitors (OSCI) on the growth of bacteria and its corrosion inhibition efficiency were investigated. Corrosion inhibition efficiency was studied by rotating cage test and the nature of biodegradation of corrosion inhibitor was also analyzed by using FTIR, NMR and GC-MS. This isolate has the capacity to degrade the aromatic and aliphatic hydrocarb...

After the rapid growth in the use of CoCrMo metal-on-metal hip replacements since the second generation was introduced circa 1990, metal-on-metal hip replacements have experienced a sharp decline in the last two years due to biocompatibility issues related to wear and corrosion products. Despite some excellent clinical results, the release of wear and corrosion debris and the adverse response o...

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corros...

Divalent cationic strontium (Sr2~-l adsorption to and desorption from iron corrosion products were examined in two model drinking water distribution systems (DWDS). One system was maintained with chlorine-disinfected drinking water and the other with the same water with secondary chloramine disinfection. Flow conditions simulated primary transmission lines (constant flow) and residential mains ...