The kinetics and mechanism of bainite transformation have been studied in Fe-Cr-Mo-V-Ti-C steel high speed dilatometry backed by thermodynamic analysis. The complete transformation of austenite, however, has not occurred at any reported temperature. Obtained results confirm the incomplete reaction phenomenon with the cessation of the bainite transformation well before the paraequilibrium is ach...

X90 pipeline steel was processed with the simulated coarse grain heat affect zone (CGHAZ) thermal cycle with heat input varying from 30 kJ/cm to 60 kJ/cm, the microstructures were investigated by means of optical microscope (OM), scanning electron microscope (SEM), electron backscattering diffraction (EBSD), and transmission electron microscope (TEM), and the impact properties were evaluated fr...

Nanostructured bainite is a novel ultra-high-strength steel-concept under intensive current research, in which the optimization of its mechanical properties can only come from a clear understanding of the parameters that control its ductility. This work reviews first the nature of this composite-like material as a product of heat treatment conditions. Subsequently, the premises of ductility beh...

New developments with bainite have resulted in a steel with an ultimate tensile strength of 2500 MPa, a hardness of 600-670 HV and a toughness in excess of 30-40 MPa m [1]. The novel microstructure is generated in a high carbon (0.98 wt.%) high silicon (1.46 wt.%) steel austenitized for 15 min. at 1000 oC, and then isothermally transformed at temperatures of ∼200 oC. Iron does not diffuse durin...

The relationship between alloying content, microstructure and properties has been studied for high strength steel weld metals with 7 to 9 wt. % nickel. Neural network modelling suggested that manganese reductions lead to large impact toughness increases and that nickel must be added in a controlled manner with respect to manganese in order toincrease impact toughness. Carbon additions were pred...

We investigated the effects of the additions of Zr and other alloying elements on the mechanical properties and microstructure in Cr-Mo plastic mold steels. The addition of alloying elements changed the microstructure of the normalized samples from the upper bainite to lower bainite due to the increased hardenability. The tempering temperature influenced the strength and hardness values, especi...

Examination of a time–temperature–transformation (TTT) diagram for an eutectoid carbon steel (Fig. 1), bearing in mind the fact that the pearlite reaction is essentially a high temperature one occurring between 550C and 720C and that the formation of the martensite is a low-temperature reaction, reveals that there is a wide range of temperature ∼250–550C within which neither of these phases for...

Bainite has been obtained by heat treatment at temperatures as low as 125°C in a high carbon, high silicon steel. This has had the effect of greatly re® ning the microstructure, which is found to have a strength in excess of 2.5 GPa together with an ability to ̄ ow plastically before fracture. Such properties have never before been achieved with bainite. In this paper metallographic details are ...