Tensile specimens of nonflammable AZ91D Mg alloy were fabricated in this study via cold chamber die-casting process. Dimensions of tensile specimens were 25mm in length, 4mm in width, and 0.8 or 3.0mm in thickness. Microstructure observation was conducted before and after tensile tests at room temperature. In the die casting process, various injection distances from 150 to 260mm were employed t...

The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...

The microstructural evolution, mechanical properties, and mathematical relationship of an α, α + β, and β phase Mg-Li alloy during the cold rolling and annealing process were investigated. The results showed that the increased Li element gradually transformed the Mg matrix structure from hcp to bcc. Simultaneously, the alloy plasticity was improved remarkably during cold rolling. In the anneali...

AZ91 magnesium alloy parts were successfully produced using a novel extrusion-based additive manufacturing process. The green built in two different orientations and subjected to debindi...

A program has been conducted on the effects of Mg in cast alloy 718. The results show that small amounts of Mg improves impact toughness and decreases Nb segregation by decreasing secondary dendrite arm spacing which results in less and smaller interdendritic Laves and MC eutectics. Small amounts of Mg produce a more spheroidal as well as a more dispersive MC phase. Impact toughness was found t...