UNLABELLED Clinicians tend to make reductions in glass ionomer power/liquid (P/L) ratios since some materials are difficult to mix and flow into small cavities, grooves or pits. In general, changing the P/L ratio decreases the physical and mechanical properties of conventional glass ionomer cements (GICs) and resin modified glass ionomer cements (RMGICs), but alterations seem to depend on their...

white spot lesions are observed in nearly 50% of patients undergoing orthodontic treatment. long-lasting antibacterial properties of orthodontic cements can reduce this phenomenon. the aim of this research was to compare antimicrobial activity of three commercial glass ionomer cements with three commercial zinc phosphate cements, over time, against streptococcus mutans and candida albicans. dir...

statement of the problem : tooth restorations are exposed to stresses which produce marginal gaps resulting in microleakage. purpose in this study, microleakage of light-cured glass-ionomer and compomer class v restorations was evaluted and compared under cyclic loading materials and methods in this exprimental study, class v cavities were prepared on the buccal surfaces of maxillary premolars ...

The purpose of this study was to evaluate the surface roughness of four conventional chemically cured glass ionomer cements (Fuji IX, Ketac Molar, Vidrion R and Vitromolar) commonly used in atraumatic restorative treatment (ART) immediately after material preparation. Twenty specimens of each glass ionomer cement were fabricated and surface roughness was measured after material setting. The spe...

This in vitro study assessed the marginal microleakage on class V cavities prepared with aluminum oxide air abrasion and restored with different glass ionomer cements. The cavities were prepared on the buccal and lingual surfaces of 15 sound third molars with an air- abrasion device (Kreativ Mach 4.1; New Image) using a 27.5-microm aluminum oxide particle stream, and were assigned to 3 groups o...

Introduction: Radiopacity is a necessary property for luting cements . The aim of this study was to investigate the radiopacity of some luting dental cements used in prosthetic dentistry. Methods: Five disclike samples of each material (6 x 1 mm) were prepared from panavia F2.0(Pa), Chioce2 (Ch.2), Glass ionomer GC (GI GC), zinc phosphate Hoffmann’s (ZP hof), zinc polycarboxylate Hoffm...

BACKGROUND There are a number of studies citing the primary reason for replacing auto cure glass ionomer cements was due to recurrent caries. The purpose of this study was to use an in vitro model to measure caries at the dentine restoration interface of bonded composite resin and auto cure glass ionomer cement restorations and to measure the amount of surface degradation occurring in the resto...

Fluoride release into deionized water from two glass-ionomer cements (Aqua Ionofil and Ceramfil β) and two polyacid-modified composite resins or compomers (Hytac and Dyract AP) was examined over different time periods. Nine cylindrical specimens (2.5 x 8.5 mm) of each material were prepared and allowed to stand in deionized water. The resulting solutions were analyzed for fluoride by the Alizar...

The purpose of this study was to evaluate the genotoxic potential of components leached from two conventional self-curing glass-ionomer cements (Fuji IX and Ketac Molar), and light-curing, resin modified glass-ionomer cements (Vitrebond, Fuji II LC). Evaluation was performed on human lymphocytes using alkaline and hOGG1 modified comet, and micronucleus assays. Each material, polymerised and unp...