With the increasing prevalence of polymer composites in engineering applications, invariably mechanical failures of these components are occurring. Key to addressing this is fractographic analysis; the examination of fracture surfaces to deduce information about the damage and failure of components. The fractography of isotropic materials, particularly metals, has been used as a tool for many y...

Stress corrosion cracking (SCC) behavior of Ni-free duplex stainless steels containing N and C (Febalance-19Cr-8Mn-0.25C-(0.03, 0.21)N, in wt %) was investigated by using a slow strain rate test (SSRT) in air and aqueous NaCl solution with different tensile directions, including parallel (longitudinal) and perpendicular (transverse) to the rolling direction. It was found that alloying N was eff...

Diamond coating of suitable template materials and subsequent delamination allows for the manufacturing of free-standing diamond foil. The evolution of the microstructure can be influenced by secondary nucleation via control of process conditions in the hot-filament chemical vapour deposition process. Bending tests show extraordinarily high strength (more than 8 GPa), especially for diamond foi...

The article deals with the analysis of structure and fracture surface aluminum alloy samples. Alu-minum AlMg9 was used as an experimental material. material from which samples were made supplied cast without heat treatment, specifically produced by continuous casting method. test examined using a Neophot 32 optical microscope, sample scanning electron microscope (SEM). fatigue life tested three...

The effects of cryogenic temperature on the toughness of a Zr-based metallic glass are investigated. Based on three-dimensional fracture morphologies at different temperatures, the crack formation and propagation are analyzed. Through the calculation of the shear transformation zone volume, the shear modulus and bulk modulus of the metallic glass at different temperatures and the crack formatio...