Isolated FePt particles were fabricated by taking advantage of overgrowth of Fe on Pt particles and subsequent annealing at 873K. The annealing lead to the formation of ordered tetragonal (L10) FePt particles with three orthogonal variants. The average size of FePt particles could be adjusted to less than 10 nm and no significant grain coarsening occurred upon annealing due to the existence of ...

The chemical reduction of ferric acetylacetonate (Fe(acac)₃) and platinum acetylacetonate (Pt(acac)₂) using the polyol solvent of phenyl ether as an agent as well as an effective surfactant has successfully yielded monodispersive FePt nanoparticles (NPs) with a hydrophobic ligand and a size of approximately 3.8 nm. The present FePt NPs synthesized using oleic acid and oleylamine as the stabiliz...

A one-step synthesis of FePt nanoparticles is reported. The size, composition, and shape of the particles are controlled by varying the synthetic parameters such as molar ratio of stabilizers to metal precursor, addition sequence of the stabilizers and metal precursors, heating rate, heating temperature, and heating duration. An assembly of large (6 nm or greater) FePt nanoparticles, especially...

In this study, multifunctional hybrid nanoparticles composed of iron platinum (FePt), silica (SiO2), and gold nanoparticles (AuNPs) had been developed for surface-enhanced Raman scattering (SERS) application. Core-shell structure of SiO2 and FePt nanoparticles (FePt@SiO2) was fabricated through sol-gel process and then immobilized gold nanoparticles onto the surface of FePt@SiO2, which displays...

The effects of TiN-ZrO₂ intermediate layer on the microstructures and magnetic properties of FePt films were investigated. The TiN-ZrO2 intermediate layer was granular consisting of grains of solid solution of Ti(Zr)ON segregated by amorphous ZrO₂. By doping ZrO₂ into TiN intermediate layer, the FePt grains became better isolated from each other and the FePt grain size was reduced. For 20 vol. ...

In this study, the mechanisms for the formation of FePt nanocubes via pyrolysis of iron pentacarbonate [Fe(CO)5] and platinum(II) acetylacetonate [Pt(acac)2] were investigated. The time evolution of the structure, morphology, and composition of the FePt nanocubes was probed by transmission electron microscopy (TEM) at different reaction stages. On the basis of the detailed characterization, we ...

FePt-Ag nanocomposite films with large perpendicular magnetic anisotropy have been fabricated by alternate-atomic-layer electron beam evaporation onto MgO(100) substrates at the low temperature of 300 °C. Their magnetization behavior and microstructure have been studied. The surface topography was observed and varied from continuous to nanogranular microstructures with insertion of Ag nanolayer...

FePt nanoparticles with average size of 9 nm were synthesized using a diblock polymer micellar method combined with plasma treatment. To prevent from oxidation under ambient conditions, immediately after plasma treatment, the FePt nanoparticle arrays were in situ transferred into the film-growth chamber where they were covered by an SiO2 overlayer. A nearly complete transformation of L10 FePt w...

To obtain the optimal 1:1 composition of FePt alloy nanomaterials by polyol synthesis, the iron precursor (iron pentacarbonyl, Fe(CO)5) must be used in excess, because the Fe(CO)5 exists in the vapor phase at the typical temperatures used for FePt synthesis and cannot be consumed completely. Fabrication of Fe3O4 nanoparticles by consuming the excess iron precursor was an effective strategy to m...