The effect of tension-tension fatigue (T-T) on carbon/epoxy composites (CFC) has been investigated in this paper. Load controlled fatigue tests were conducted in the tension-tension (T-T) cyclic mode with the R-ratio values of 0.1 and 0.3 and subsequently the specimens with the fatigue life over 10 cycles have been studied by means of tensile testing, ultrasonic inspection and quantitative data...

By taking the axial tension member as an example, the damage caused by the cyclic stress influencing reliability was researched. According to the damage mechanics theory, some micro-cracks were observed in the material with cyclic load. With the increase of times loads inflicting, the fresh micro-cracks were formed; meanwhile, the existing cracks further extended, consequently, the effective be...

Cyclic AMP is the prototypical second messenger of beta-adrenergic receptors, but recent findings have questioned its role in mediating smooth muscle relaxation upon beta-adrenergic receptor stimulation. We have investigated the signaling mechanisms underlying beta-adrenergic receptor-mediated relaxation of rat urinary bladder. Concentration-response curves for isoproterenol-induced bladder rel...

The tension–tension fatigue behavior of (the layer-to-layer) three-dimensional angle-interlock woven composite (3DAWC) was investigated using the acoustic emission (AE) technique, examination of damaged regions via light microscopy and micro-CT, and finite element analysis (FEA). AE events occurred during the entire fatigue process, and damage modes were determined based on cumulative fatigue d...

In this paper, a Paris law-based model is presented whereby crack propagation occurs under cyclic loading in air (fatigue) and in an aggressive environment (corrosion-fatigue) for the case of corner cracks (with a wide range of aspect ratios in the matter of the initial cracks) in finite-thickness plates of 316L austenitic stainless steel subjected to tension, bending, or combined (tension + be...