condensation reaction of urea, casein and formaldehyde in the presence of varying proportion of resorcinol under alkaline condition. All the prepared resins were characterized by free-formaldehyde content, free-phenol content, viscosity measurements and infrared spectroscopy (IR). The resin samples were cured isothermally at 120oC using two different curing agents, p-toluene sulphonic acid (PTS...

Lignocellulosic fibers have received much more attention than ever before from the research community all over the world during the past few years because of their enormous advantages. A study on the preparation of new series of polymer composites using Pine Needles as a reinforcing material in Urea Formaldehyde resin has been made. Mechanical properties of intimately mixed particle reinforced ...

In this study, nanocrystalline cellulose (NCC) was used for increasing the bonding strength of urea-formaldehyde (UF) resin adhesive, with a reduction of formaldehyde (HCHO) emissions. The surface of NCC was modified by 3-aminpropyltriethoxysilane (APTES) and 3-methacryloxypropyltrimethoxysilane (MPS) for the lack of compatibility with UF resin adhesive. The modified NCC was characterized by X-...

The objective of this study is to evaluate the effect of décor paper and resin type on physical properties, mechanic properties, and surface quality properties of particleboards coated with décor papers impregnated by using different resin. White oak, New wenge and common maple pattern decor papers impregnated with urea formaldehyde (UF), melamine formaldehyde (MF) and urea-melamine formaldehyd...

Urea formaldehyde resins were formulated with vatiables of three reaction pHs (1.0, 4.8, and 8.0 5.0) and three catalysts (sodium hydroxide, sodium hydroxide/ammonium mix, and triethanolamine) . The resins were prepared by placing all formaldehyde and water in reaction kettle and pH was adjusted with sulfnric acid and sodium hydroxide, respectively. Urea was added in 1.5 equal parts at 1 minute...

Abstract Soy flour can be substituted in polymeric diphenylmethane diisocyanate (pMDI) resin for bonding plywood. Resin bleed-through is avoided by prepressing at 95°C. The boards have greater wet and dry strength than do those prepared from melamine-urea-formaldehyde (MUF) resin. also emulsion polymer isocyanates cold-press applications. soy increases but keeps the unchanged. optimal level of ...

The objective of this study was to improve interfacial adhesion properties at the interface of thermomechanical pulp (TMP) fiber and isotactic polypropylene (iPP) using thermoset adhesives such as phenol formaldehyde (PF) and urea formaldehyde (UF). This study also attempted to achieve fiber-to-fiber adhesion using thermoset adhesives before the molten iPP would flow into the fiber web. The fra...