The purpose of this study was to construct a flowmeter that could accurately measure the hydraulic permeability of electrospun fibrinogen scaffolds, providing insight into the transport properties of electrospun scaffolds while making the measurement of their topographical features (fiber diameter and pore size) more accurate. Three different concentrations of fibrinogen were used (100, 120, an...

Plasma sputtering deposition of Platinum thin films is studied on porous anodic aluminum oxide (AAO) template. The size effect of AAO cylindrical pores is shown to influence the diffusion of atoms in the porous layer. The resulting maximum reached depth of platinum varied from 2 μm to 20 μm, and the density on the surface is lowered from 23 μg.cm to 5 μg.cm as the pore diameter increased from 4...

We report a new method for the fabrication of sub-10 nm nanopores in a fast single process step. The pore formation is accomplished by exploiting the competition between sputtering and deposition in ion-beam-induced deposition (IBID) on a thin membrane. The pore diameter can be controlled by adjusting the ion beam and gas exposure conditions. The pore diameter is well below the limit that can b...

In this letter, the uniform 4H silicon carbide (SiC) mesopores was fabricated by pulsed electrochemical etching method. The length of the mesopores is about 19 μm with a diameter of about 19 nm. The introduction of pause time (T off) is crucial to form the uniform 4H-SiC mesopores. The pore diameter will not change if etching goes with T off. The hole concentration decreasing at the pore tips d...

Mesoporous nanostructured γ-Al2O3 powders were synthesized through multi- step precipitation procedures using the pH-swing technique. Structural and morphological characteristics in addition to the thermal behavior of the procured samples were characterized via X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), fourier transform infrared (FT-IR) ...

Mesoporous nanostructured γ-Al2O3 powders were synthesized through multi- step precipitation procedures using the pH-swing technique. Structural and morphological characteristics in addition to the thermal behavior of the procured samples were characterized via X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), fourier transform infrared (FT-IR) ...

in this work, a tracer study on pore initiation in anodic alumina in oxalic acid was performed. effects of some experimental parameters such as applied electrical potential, electrolyte composition and heat pretreatment were evaluated. electrochemical and morphological experiments were performed using potentiostatic anodizing and scanning electron microscopy (sem) techniques, respectively. effe...

Porous carbon materials with pore sizes from 3 to 200 nm were synthesized by reacting hexafluorobenzene with Na liquid at 623 K. NaF crystals, a byproduct formed in the reaction, acted as nanotemplate to assist the pore formation. By employing hexafluorobenzene to react with Na incorporated within the channels (diameter 200 nm) of anodized aluminum oxide (AAO) membranes at 323-623 K, the carbon...