A polyelectrolyte nanoparticle composed of PEG-PLL(-g-Ce6, DMA)-PLA was developed for nanomedicinal application in photodynamic therapy. These nanoparticles formed stable aggregates through the hydrophobic interaction of poly(lactic acid) and demonstrated pH-dependent behaviors such as surface charge conversion and enhanced cellular uptake at acidic pH, resulting in improved phototoxicity. In v...

In this research an attempt is made to modify the brittle poly (Lactic acid) (PLA) into flexible PLA by adding Poly (Butylene Succinate) (PBS), Poly (Ethylene Glycol) (PEG) and Ricinoleic acid (R.ACID) as a plasticizer. Various plasticizers with different weight % of plasticizers 10%, 20% and 30% in wt% for PLA/PBS, 5, 10 and 15% for PLA/PEG and PLA/R.ACID are used to make sheets. With the addi...

Biodegradable poly(L-lactic acid) (PLA) fibrous scaffolds were prepared by electrospinning from a PLA melt containing poly(ethylene glycol) (PEG) as a plasticizer to obtain thinner fibers. The effects of PEG on the melt electrospinning of PLA were examined in terms of the melt viscosity and fiber diameter. Among the parameters, the content of PEG had a more significant effect on the average fib...

In this work, biotin surface functionalized hydrophilic non-water-soluble biocompatible poly(lactic acid) (PLA) nanofibers are created for their potential use as biosensors. Varying concentrations of biotin (up to 18 weight total percent (wt %)) were incorporated into PLA fibers together with poly(lactic acid)-block-poly(ethylene glycol) (PLA-b-PEG) block polymers. While biotin provided surface...

Kenaf bast fiber (KBF) filled plasticized poly(lactic acid) (p-PLA) composites was prepared and examined stage by stage in this study. Firstly, poly(lactic acid) (PLA) was plasticized with 5 up to 20 wt% poly(ethylene glycol) (PEG) via internal mixer. Blend with 10 wt% PEG was chosen as matrix for composite as it showed the best impact strength and elongation at break. Secondly, maleic anhydrid...

PEG–PLA hydrogels were prepared by stereocomplexation of poly(lactide) (PLA) blocks of opposite chirality. Gelation occurred upon mixing aqueous solutions of both enantiomers of PEG6500–(PLA)2, PEG12500–(PLA)2 and PEG21800–(PLA)8 block copolymers. Stereocomplexed hydrogels from PEG6500–(PLA)2 polymers were found to be stable up to ~37 8C, while those from PEG12500–(PLA)2 and PEG21800–(PLA)8 blo...

We have recently reported our study on novel nano-dimension red blood cell (rbc) substitute based on ultrathin PEG-PLA membrane nanocapsules (80-150 nanometer diameter) containing hemoglobin (Hb) and enzymes. These have a markedly increased the circulation half-times as compared to our earlier PLA membrane nanocapsules. In the present study to be reported here, instead of looking at this from a...

Post-coating of biodegradable polylactides (PLA)/polyethylene glycol (PEG) microspheres with a gelatin film produced by dipping the microspheres into a gelatin solution to reduce the initial drug release burst was investigated. Biodegradable block PLA/PEG microspheres, prepared by w/o emulsion/solvent evaporation, showed that the hydrophilic segment PEG protruded to the sphere surface. However,...

To achieve sustained release of 3-ethyl-4-(4-methylisoxazol-5-yl)-5-(methylthio) thiophene-2-carboxamide (BFB0261), a new potent osteogenic compound for treating bone disorders, we prepared film formulations containing BFB0261 and the following newly synthesized biodegradable polymers by a solvent casting technique: poly(D,L-lactic acid) (PLA), poly(D,L-lactic acid-co-glycolic acid) (PLGA), pol...