Fe-Ni-Cr austenitic alloys are widely used in hydrogen environments as structural materials. Their weld normally shows higher hydrogen-embrittlement sensitivity than the base metal, endangering large-scale applications. Herein, by using electron microscopy and numerical calculations, influence of applied load on fracture mode hydrogen-embrittled JBK-75 alloy weldment is revealed correlated with...

In high-strength steels it is often difficult to distinguish between hydrogen embrittlement and various other brittle failure mechanisms. The objective of this work was to develop a sensitive analytical procedure based on secondary ion mass spectrometry (SIMS) that would allow in-service identification of local hydrogen accumulation, either during quality control or during failure analysis of e...

Intergranular cracking associated with hydrogen embrittlement represents a particularly severe degradation mechanism in metallic structures which can lead to sudden and unexpected catastrophic fractures. As a basis for a strategy for the prognosis of such failures, here we present a comprehensive physical-based statistical micro-mechanical model of such embrittlement which we use to quantitativ...