CaO-P(2)O(5) glasses with additions of MgO and CaF(2) were used as a sintering aid of hydroxyapatite, and glass-reinforced hydroxyapatite composites obtained. Glasses promoted significant changes in the microstructure of the composites, namely with the formation of tricalcium phosphate secondary phases, beta and alpha-TCP. Quantitative phase analysis was performed by the Rietveld method using G...

For bone regeneration and repair, combinations of different materials are often needed. Biodegradable polymers are often combined with osteoconductive materials, such as bioactive glass (BaG), which can also improve the mechanical properties of the composite. The aim of this work was to develop and characterize BaG fiber reinforced starch-poly-epsilon-caprolactone (SPCL) composite. Sheets of SP...

Polyamide 6 (PA6) and short glass fiber (SGF) reinforced PA6 composites toughened with glycidylisobutyl oligomeric silsesquioxane (G-POSS) and 1.10-carbonyl-bis-caprolactam (CBC) were prepared by meltextrusion compounding process and then compounds were formed to 2 mm thick double edge notched tension samples (DENT) by injection moulding process. Fracture properties of composites were analyzed ...

Surface modifications of glass-reinforced hydroxyapatite composites immersed in a simulated physiological solution were studied using X-ray photoelectron spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. In the first stages of the apatite formation process, calcium and silicon ions were leached out from the surface of the composites. After 12 days of immersion...

The knowledge of load bearing characteristics and failure of material is very important for mechanical engineers. Various metallic, non metallic and composite materials are used in different application. In view of this, the main objective of the present work is to analyze the influence of Aluminum Oxide filler on Fracture Toughness properties of Chopped Strand Mat (CSM) E-Glass Fiber reinforce...

The influence of fiberlmatrix interactions on the mechanical behavior of ceramic matrix composites is examined on glass matrix composites and mainly on composites made by chemical vapor infiltration (CVI) of a fiber preform by a SiC matrix. Then the relationships between interfaces and features of the stress-strain behavior are highlighted on microcomposite specimens using experimental data and...

To increase the toughness of a metallic glass with the nominal composition Zr57Nb5Al10Cu15.4Ni12.6, it was used as the matrix in particulate composites reinforced with W, WC, Ta, and SiC. The composites were tested in compression and tension experiments. Compressive strain to failure increased by more than 300% compared with the unreinforced Zr57Nb5Al10Cu15.4Ni12.6, and energy to break of the t...

Milling of fiber reinforced polymer composites is of great importance for integrated composites with other mating parts. Improper selection of cutting process parameters, excessive cutting forces and other machining conditions would result in rejection of components. Therefore, machining conditions are optimized to reduce the machining forces and damages. This work reports practical experiments...

Results of an investigation of the mechanical performance of injection moulded long glass fibre reinforced polyamide 6,6 composites are presented. The glass fibre content in these composites was varied over the range 10-50% by weight using fibres with average diameters of 10, 14, and 17 micrometres. Mechanical testing and analysis of the apparent interfacial shear strength was carried out at 23...