Estimating and tracking crack growth dynamics is essential for fatigue failure prediction. A new experimental system— coupling structural and crack growth dynamics—was used to show fatigue damage accumulation is different under chaotic (i.e., deterministic) and stochastic (i.e., random) loading, even when both excitations possess the same spectral and statistical signatures. Furthermore, the co...

background: supplementation usage approach and its effect on fatigue retarding had been focused on by athletes and coaches. the aim of this study was to compare the effect of two acute and chronic loading of sodium bicarbonate supplement on lactate and inflammatory indices after exhaustive aerobic activity in active men. method s : 10 active men were selected and assigned to experimental group....

This article presents the strain-based experimental data for Ti-6Al-4V ELI under non-constant amplitude cyclic loading. Uniaxial strain-controlled fatigue experiments were conducted under three different loading conditions, including two-level block loading (i.e. high-low and low-high), periodic overload, and variable amplitude loading. Tests were performed under fully-reversed, and mean strain...

It is difficult to conduct cyclic tensile fatigue tests for fine ceramics because of its high brittleness, and a little eccentricity of loading axis and gripping device gives inaccurate strength data. So, a major part of cyclic fatigue tests have been carried out under bending load conditions, for the allowance of misalignment of loading axis is generous to some extent in the case of bending fa...

Low cycle fatigue–creep is the main reason for the failures of many engineering components under high temperature and cyclic loading. Based on the exhaustion of the static toughness and dissipation of the plastic strain energy during fatigue failure, a new low cycle fatigue–creep life prediction model that is consistent with the fatigue–creep damage mechanism and sensitive to the fatigue damage...

The role of crack-tip shielding in in ̄uencing mixed-mode (mode I‡ II) fatigue-crack growth thresholds for large, through-thickness cracks in a Ti±6Al±4V turbine blade alloy is examined under high-cycle fatigue loading conditions, i.e., at a loading frequency of 1000 Hz in ambient temperature air for load ratios (Kmin=Kmax) of R ˆ 0:1±0.8. Techniques are developed to quantify crack-tip shielding...

BACKGROUND Fatigue damage of the long bones is prevalent in running athletes and military recruits due to vigorous mid- and long-term physical activity. The current study attempted to know the features of bony athletic fatigue damage and to explore the mechanism of fatigue damage repair through bone targeted remodeling process. METHODS Right ulnae of the Wistar rats were fatigue loaded on an ...

In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...

Finite element analysis of a tubular T-joint subjected to various loading conditions including pure axial loading, pure in-plane bending (IPB) and different ratios of axial loading to in-plane bending loading has been carried out. This effort has been established to estimate magnitudes of the peak hot spot stresses (HSS) at the brace/chord intersection and to find the corresponding locations as...