OBJECTIVES The study is to evaluate changes in microhardness of enamel after exposure to acidic center filled chewing gum on primary and permanent teeth. METHODS Thirty primary and 30 permanent molar extracted teeth were painted with acid resistant varnish except a small window over buccal surface. Teeth were divided into four groups according to type of teeth and type of chewing gum (Center ...

Acid erosion is a superficial loss of enamel caused by chemical processes that do not involve bacteria. Intrinsic and extrinsic factors, such as the presence of acid substances in the oral cavity, may cause a pH reduction, thus potentially increasing acid erosion. The aim of this study was to evaluate the microhardness of bleached and unbleached bovine enamel after immersion in a soda beverage,...

PURPOSE The aim of the present study was to evaluate the alterations of surface microhardness and wear caused by the sodium bicarbonate jet on bovine enamel and the further remineralizing effect of artificial saliva. METHODS Fifteen enamel samples (4,0mm x 4,0mm) were used, which constituted the groups: no treatment (MI); treatment with sodium bicarbonate jet (MII and DI); treatment with sodi...

The aim of this study was to evaluate in vitro and in situ the effects of two bleaching treatments on human enamel surface microhardness. Sixty enamel slabs from recently extracted thirty molars were used. The specimens were polished with sandpapers under water-cooling. The enamel samples were randomly divided in four groups, treated with 10% hydrogen peroxide (HP) or Whitening Strips (WS) cont...

BACKGROUND According to the guideline of the United States center for disease control (CDC), the extracted teeth should be sterilized by autoclaving or storage in 10% formalin before using for educational or research purposes. The objective of this study was to evaluate the effect of this protocol on microhardness of dentin and enamel. MATERIAL AND METHODS Thirty extracted single-root teeth w...

Received for publication: Sep. 06, 2007. Revised: Sep. 21, 2007. rEZUMat 1 Department of Oral Rehabilitation and Dental Emergency, Faculty of Dentistry, Victor Babes University of Medicine and Pharmacy, Timisoara, 2 Department of Material Sciences and Thermal Treatments, Faculty of Mechanical Engineering, Polytechnic University, Timisoara, 3 Department of Dental Materials and Dental Technologie...

Introduction: Many patients seeking orthodontic treatment already have incipient enamel lesions and should be placed under preventive treatments. The aim of this in vitro study was to evaluate the effect of CPP-ACP paste and CO2 laser irradiation on demineralized enamel microhardness and shear bond strength of orthodontic brackets. Methods: Eighty caries-free human premolars were subjected t...

BACKGROUND This study evaluated the effects of the acids used in the microabrasion on enamel. MATERIAL AND METHODS Seventy enamel/dentine blocks (25 mm2) of bovine incisors were divided into 7 groups (n=10). Experimental groups were treated by active/passive application of 35% H3PO4 (E1/E2) or 6.6% HCl (E3/E4). Control groups were treated by microabrasion with H3PO4+pumice (C5), HCl+silica (C...

Background: To evaluate and compare the microhardness of deciduous teeth treated with nano-hydroxyapatite and calcium sucrose phosphate after iron drop exposure. Material and Methods: Twenty healthy anterior deciduous teeth were collected and stored in 0.9% saline solution at room temperature. All the teeth were immersed in artificial saliva in an incubator shaker at 37° for an hour and then su...

objective: this study aimed to assess the destructive effects of citric acid, lactic acid and acetic acid produced from the fermentation of foods on primary teeth enamel.   methods: this in vitro, experimental study was conducted on 24 sound primary teeth. the teeth were polished with a fine abrasive paper under running water. tooth pieces measuring 3 × 4 × 3mm were cut out of the teeth and sto...