Understanding the mechanism of fracture is essential for material and process design. While the initiation of fracture in brittle solids is generally associated with the preexistence of material imperfections, the mechanism for initiation of fracture in viscoelastic fluids, e.g., polymer melts and solutions, remains an open question. We use high speed imaging to visualize crack propagation in e...

We investigate theoretically statistics and thermally activated dynamics of crack nucleation and propagation in a two-dimensional heterogeneous material containing quenched randomly distributed defects. We consider a crack tip dynamics accounting for dissipation, thermal noise and the random forces arising from the elastic interactions of the crack opening with the defects. The equation of moti...

In this letter, the quantity effect of radial cracks on the cracking propagation behavior as well as the circular crack generation on the impacted glass plate within the sandwiched glass sheets are experimentally investigated via high-speed photography system. Results show that the radial crack velocity on the backing glass layer decreases with the crack number under the same impact conditions ...

Crack propagation in an isotropic 2d brittle material is widely viewed as the interplay between two separate criteria. Griffith’s cap on the energy release rate along the crack path decides when the crack propagates, while the Principle of Local Symmetry PLS decides how, that is, in which direction, that crack propagates. The PLS, which essentially predicts mode I propagation, cannot possibly h...

We investigate the process of slow intergranular crack propagation by the finite element method model and show that branching is induced by partial arresting of a crack front owing to the geometrical randomness of grain boundaries. A possible scenario for the branching instability of crack propagation in a disordered continuous medium is also discussed.

this study investigates propagation of mode i crack in b70 pre-stressed concrete sleepers by fracture mechanics approach. a new experimental analysis is done for notched b70 pre-stressed concrete sleepers with replica test and image analysis. a scanning electron microscope test (sem) and an image analysis are applied for the replica test in order to determine crack length and crack mouth openin...

We have carried out systematic fracture experiments in a single edge notch geometry over a range of stretch rates on dual crosslink hydrogels made from polyvinyl alcohol chains chemically crosslinked with glutaraldehyde and physically crosslinked with borate ions. If the energy release rate necessary for crack propagation was calculated conventionally, by using the work done to deform the sampl...

Static fatigue behavior is the main failure mode of optical fibers applied in sensors. In this paper, a computational framework based on continuum damage mechanics (CDM) is presented to calculate the crack propagation process and failure time of optical fibers subjected to static bending and tensile loads. For this purpose, the static fatigue crack propagation in the glass core of the optical f...

We present a combined novel methodology to study the three-dimensional complex geometry of a tortuous crack and identify the essential features of the crack and its propagation inside a heterogeneous material. We find that some severe damage events occur unexpectedly below a local mode-I crack within the sample; we realize that the severe plastic zone of the local mode-I crack is shifted down b...

In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...