The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...

The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O2 flow at 600 ̋C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and...

The increase in CO2 concentrations and global warming will increase the carbonation depth of concrete. Furthermore, temperature rise will increase the rate of corrosion of steel rebar after carbonation. On the other hand, compared with normal concrete, high volume fly ash (HVFA) concrete is more vulnerable to carbonation-induced corrosion. Carbonation durability design with climate change is cr...

tarnish and corrosion behavior of three commercial dental amalgams namely am.1, am.2, am.3, have been investigated by utilizing in vitro tests. the corrosion and/or dissolution rate of the three dental amalgams were studied in 0.9 wt% nacl solution, artificial saliva and ringers solution. potentiodynamic polarization technique was employed to study cathodic and anodic polarization behavior, fro...

Biofilm formation is one of the major problems of recirculating cooling water systems which detriments the life of equipment, through biocorrosion or microbiologically influenced corrosion (MIC). Sulfate reducing bacteria (SRB) are considered to be the major bacterial group involved in MIC. In the present study, SRB cultures are isolated from aeration basin inlet water sample of cooling water s...

Investigations were conducted on hot corrosion of Nickel base, NIMONIC-90 at 675°C and 725°C. The tests were carried out on small test coupons coated with a chemical containing Sodium sulphate and Sodium Vanadate which is representative of the corrosive deposit that usually forms during service in the coal fired boiler and the likes operating in marine atmospheres. Corrosion rates were measured...

Glass cell experiments were conducted to investigate the mechanism and kinetics of mild steel corrosion in H2S environments which is accompanied by iron sulfide scale formation. By using the weight change method, the rates of corrosion and scale formation were found. It was also concluded that mackinawite is the predominant type of iron sulfide that formed on the steel surface under the test co...

The high-velocity oxygen-fuel (HVOF) spraying process was used to fabricate conventional WC-10Co-4Cr coatings and FeCrSiBMn amorphous/nanocrystalline coatings. The synergistic effect of cavitation erosion and corrosion of both coatings was investigated. The results showed that the WC-10Co-4Cr coating had better cavitation erosion-corrosion resistance than the FeCrSiBMn coating in 3.5 wt.% NaCl ...

Corrosion behavior of solution annealed high-carbon and low-carbon CoCrMo wrought alloy, commonly used in medical joint implants, was investigated. The surface passivation properties remained similar with and without the various solution anneal conditions, while the rate of corrosion was lower for solution annealed high-carbon CoCrMo. Corrosion was found to target phase boundaries and certain g...

Corrosion behavior of two multiphase Mg-Li-Al-based alloys in 0.6 M NaCl aqueous solution is investigated by hydrogen gas evolution measurement and electrochemical test. This paper reports, for the first time, the comparison of hydrogen evolution and Tafel extrapolation results of Mg-Li-Al-based alloys. The corrosion rate of Mg-9Li-7Al-1Sn is observed to be reasonably higher when compared to th...