The aim of this study was to investigate the effect of inhibition of Marrubium astranicumleaves extract on the corrosion of carbon steel in hydrochloric acid solution by using weightloss and tafel polarization methods. Inhibition was found to increase with increasingconcentration of the leaves extract. The inhibition efficiency of this extract at an optimumconcentration of 100 mg L-1 was 99.9 %...

The effect of Mentha spicata L. extract on the corrosion behaviour of carbon steel in 1.0 M HCl solution was investigated using polarization, electrochemical impedance spectroscopy (EIS) and electrochemical noise (EN) techniques. The solution containing 250 ppm of the ethanolic solution of extract showed the highest inhibition efficiency (IE). The effect of temperature on the rate of corrosion ...

acid extract of solanum tuberosum was tested as corrosion inhibitor for mild steel in 1 m hcl and h2so4 media using different techniques: weight loss (in different temperatures viz., 303, 313 and 323 k), potentiodynamic polarization, electrochemical impedance spectroscopy (eis) and sem techniques. the studies reveal that the plant extract act as good inhibitors in both the acid media and better...

treated sea water is the most significant source of water and surfactant floods. the various chemicals employed in treatment plants should be compatible with surfactant systems. based on surface tension experiments, the activity of these chemicals is examined over a wide range of concentrations in different solutions, including distillated water, sea water by using three types of surfactant mix...

Vanillin is an interesting corrosion inhibitor because of its safe use and high solubility inwater. The effect of vanillin on the corrosion inhibition of carbon steel in 1.0 Mhydrochloric acid solution has been studied using potentiodynamic polarization,electrochemical impedance spectroscopy (EIS) and electrochemical noise (EN) techniques.The effect of temperature on the rate of corrosion in th...

In this study, the ability of lithium nitrite and amino alcohol inhibitors to provide corrosion protection to reinforcing steel was investigated. Two types of specimens-reinforcing steel and a reinforced concrete prism that were exposed to chloride ion levels resembling the chloride attack environment-were prepared. An autoclave accelerated corrosion test was then conducted. The variables teste...

This study set out to examine the cystoseira gibraltarica extract (CG) as an environmentally sustainable corrosion inhibitor for carbon steel in 1.0 M HCl medium. The corrosion inhibiting effect has been studied by conventional methods such as gravimetric (weight loss) and electrochemical (EIS and PDP) methods. All the methods used in this study confirm that cystoseira gibraltarica extract has ...

The self-assembled monolayer (SAM) was prepared using octadecyl trichlorosilane (OTS) in distilled solution on the copper surface. The effect of inhibitor concentration on the rate of inhibition efficiency and corrosion rate in corrosion medium on copper by using polarization curves, electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) was studied. The results showed...

A corrosion inhibitor is a chemical substance which, when added in small concentrations to an environment, minimizes or prevents corrosion [I]. Corrosion inhibitors are used to protect metals from corrosion, including temporary protection during storage or transport as well as localized protection, required, for example, to prevent corrosion that may result from accumulation of small amounts of...

Treated sea water is the most significant source of water and surfactant floods. The various chemicals employed in treatment plants should be compatible with surfactant systems. Based on surface tension experiments, the activity of these chemicals is examined over a wide range of concentrations in different solutions, including distillated water, sea water by using three types of surfactant mix...