This paper presents the results of an experimental study on the effect of limestone powder on the compressive strength, tensile behavior, and micromechanical parameters of a highly ductile cement composite incorporating limestone powder. Four mixtures were determined according to the replacement ratio of cement with limestone powder. A series of experiments including compressive strength, uniax...

an oil and gas well cementing in gachsaran formation, where sustained annular pressure has been reported in many wells, presents a big challenge in maroon field. the main challenges are preventing gas migration and achieving zonal isolation using a competent cement sealant system which is able to withstand downhole stresses and high temperatures during production cycles. unlike conventional cem...

Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcine...

Corrosion of reinforced concrete is one of the major problems in the construction industry causing premature deterioration of concrete structures well before their service life. This has placed incredible financial burden on many projects and also placed safety of users at risk. A research work was carried out to evaluate the effect of water cement ratio on corrosion of steel in reinforced conc...

Abstract: This work was designed to investigate the simultaneous effect of both water-to-cement (W/C) and polymer-to-cement(P/C) ratios on flexural strength of type V Portland cement pastes containing polyvinyl alcohol. The obtained resultsconfirmed the strong effect of W/C-ratio on the effectiveness of the added polymer so that there exist optimum valuesfor both W/C and P/C-ratios. Pastes prep...

The ASTM C150 standard specification for Portland cement now permits the cement to contain up to 5% of ground limestone. While these and much higher levels of limestone filler substitution have been employed in Europe and elsewhere for many years, changing the ASTM standard has been a slow process. Having computational tools to assist in better understanding the influence of limestone additions...

In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...

In studies conducted to determine the workability of concrete, the bagasse ash and rice husk ash were added as a partial replacement for cement. Trial mixes with the varying water cement ratio, replacement percentage, quantity of super plasticizer and viscosity modifying agent, were prepared and tested. The results were used as the basis for defining three optimum cement replacement mix proport...

In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...

Copolymer latexes based on 2-hydroxy ethyl acrylate (2-HEA) and 2-hydroxy ethylmethacrylate (2HEMA) were synthesized with different molar ratios (95/ 05, 90/10 and 85/15) using azo-bisisobutyronitril(ABIN) as initiator and alcoholic solution as solvent. Different molar ratios of monomers was designed to investigate the effect of latexes on the physico-mechanical properties of Portland cement mo...