PURPOSE This study compared the influence of two luting cements on the clinical performance of single crowns. MATERIALS AND METHODS Twenty patients received 39 pairs of metal-ceramic and Procera crowns cemented with zinc phosphate and resin-modified glass-ionomer luting cement (Vitremer) in a split-mouth randomized pattern blinded to the recipient. The crowns were examined immediately after c...

AIM This study was undertaken to examine the effect of root canal (RT) sealers content and the cleaning procedure of RT walls on bond strength (BS) of a fiber reinforced composite (FRC) post cemented with resin-based or zinc phosphate cement. MATERIALS AND METHODS Forty bovine roots were divided into 2 groups (n = 20) and obturated with gutta-percha points plus Sealer 26 sealer or gutta-perch...

PURPOSE The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth w...

The purpose of this study was to evaluate the disintegration of luting agents. An intraoral sample holder was made having four holes of 1.4 mm diameter and 2 mm depth. The holder was soldered onto the buccal surface of an orthodontic band, which was cemented to the first upper molar in 12 patients, average age 26 years. The holes were filled with a zinc phosphate (Phosphate Kulzer), a glass ion...

introduction: the purpose of this in vitro study was to evaluate the sealing ability of the readymade temporary filling and hand mixed materials by assessing coronal microleakage. materials & methods: standardized access cavities were prepared in 80 intact human permanent premolar teeth. they were divided randomly into four experimental groups (n=20). the teeth were restored using one of the te...

OBJECTIVE This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. MATERIAL AND METHODS Sixty upper canines were decoronated and the roots were embedded in resin blocks. The ...

Results: All materials tested demonstrated different degrees of sorption and solubility. The glass ionomer cement had the best value for sorption. The zinc oxide eugenol and eugenol free cements had lower water sorption than the zinc polycarboxylate and zinc phosphate cements were evaluated. Some materials retained water in their structure and thus compensated for any loss of mass due to dissol...

phosphate, polycarboxylate, zinc oxide-eugenol and glass-ionomer products and the characteristics of these cements have been examined by several investigators2-5). In our previous investigation6), a decrease in compressive and diametral tensile strength was observed following 12 months immersion in distilled water with zinc phosphate, polycarboxylate and glass ionomer cements for luting, contai...

Background and Aim: To investigate the radiopacity of different luting, lining and filling dental cements used in prosthetic dentistry in comparison with human and bovine dental hard tissues. Material and methods: Eight cylindrical samples of each material (6 x 1 mm) were prepared from Aqualox (APC), Durelon (DE) and Adhesor Carbofine (ACF) zinc polycarboxylate cements, Cavex zinc oxide eugenol...

The dimensional changes of 4 types commercial luting cements after setting were examined in distilled water, using a developed thermal expansion testing apparatus. The measurements were carried out under three conditions: increasing temperature (from 37•Ž to 60•Ž), decreasing temperature (from 37•Ž to 10•Ž), and constant temperature (37•Ž). The results indicated that: (1) the zinc phosphate cem...