As popular aluminum alloys, the 5xxx Al-Mg series, such as 5050 and 5052, etc., are widely used in applications such as automobile, pressure vessels, armor plate, and components for marine and cryogenic service. In this, as in all non-heat-treatable aluminum alloys, the weld metal zone is considered to be the weakest part of the joint and is the location of failure when the joint is loaded in t...

Ultrasonic measurements have been performed for comprehensive microstructural characterisation in 9 % Cr ferritic steels. The variation in grain size, the effect of solution annealing temperature on microstructure developed, the variation in microstructure of the weld joints, the effect of post weld heat treatment and precipitation behaviour during thermal ageing and creep testing have been suc...

Continuous real time structural health monitoring will be a requirement for future space launch missions. Reusable metallic cryotanks manufactured using Friction Stir Welding (FSW) technology for multiple missions, demands weld and microstructural integrity. The FS weld contains multiple interfaces and a variety of microstructures. To develop NDE-based health monitoring capability which detects...

Duplex stainless steel multi-pass welds were made at 0.15 MPa, 0.45 MPa, and 0.75 MPa pressure, simulating underwater dry hyperbaric welding by the flux-cored arc welding (FCAW) method, with welds of normal pressure as a benchmark. The purpose of this work was to estimate the effect of ambient pressure on the microstructure, pitting corrosion resistance and impact toughness of the weld metal. T...

There is general agreement that a weld microstructure primarily containing acicular ferrite will exhibit high strength and excellent toughness due to its small grain size, high dislocation density, and the way in which the plates are dispersed in the microstructure (Pargeter, 1983; Sneider and Ken, 1984). In contrast, the presence of allotriomorphic ferrite, ferrite plates with aligned carbides...

A study was conducted to characterize the microstructure of electron beam welds in high purity niobium and its effect on creep behaviour at room temperature. The parent material was 2mm sheet with a 50 μm grain size. The weld fusion zone had ~ 1mm grains, implying that these grains all intersected the free surface. The parent material showed no room temperature creep deformation below the yield...