Homogeneous VO2 (B) nanorods approximately 100 nm in width and 1–2 mm in length have been fabricated via the hydrothermal process, and are then transformed into irregularly shaped V2O5 nanoparticles of several hundreds nanometers large and 20–30 nm thick after annealing the precursor material at 500 C for 30 min. Both the V2O5 sheet-like nanoparticles and VO2 (B) nanorods were tested as active ...

Numerous examples of closed-cage nanostructures, such as nested fullerene-like nanoparticles and nanotubes, formed by the folding of materials with layered structure are known. These compounds include WS2, NiCl2, CdCl2, Cs2O, and recently V2O5. Layered materials, whose chemical bonds are highly ionic in character, possess relatively stiff layers, which cannot be evenly folded. Thus, stress-reli...

Photoconductivities of monocrystalline vanadium pentoxide (V2O5) nanowires (NWs) with layered orthorhombic structure grown by physical vapor deposition (PVD) have been investigated from the points of view of device and material. Optimal responsivity and gain for single-NW photodetector are at 7,900 A W-1 and 30,000, respectively. Intrinsic photoconduction (PC) efficiency (i.e., normalized gain)...

New cerium and/or tungsten modified V2O5–TiO2 aerogel catalysts (V2O5–TiO2,V2O5–WO3–TiO2, V2O5–CeO2–TiO2 and V2O5–WO3–CeO2–TiO2) were successfully developed, by associating the sol gel procedure supercritical drying approach. A combination of various analytical techniques, including XRD, N2-Physisorption at 77 ?K, DRUV-Vis spectroscopy, NH3-TPD H2-TPR, was used to characterize obtained solids. ...

V2O5 based materials are attractive cathode alternatives due to the many oxidation state switches of vanadium bringing about a high theoretical specific capacity. However, significant capacity losses are eminent for crystalline V2O5 phases related to the irreversible phase transformations and/or vanadium dissolution starting from the first discharge cycle. These problems can be circumvented if ...

Graphene has been recognized as a promising gas sensing material. The response of graphene-based sensors can be radically improved by introducing defects in graphene using, for example, metal or metal oxide nanoparticles. We have functionalised CVD grown, single-layer graphene by applying pulsed laser deposition (PLD) of V2O5 which resulted in a thin V2O5 layer on graphene with average thicknes...

TiO2 supports doped with different amounts of Si were prepared by a sol-gel method, and 1 wt% vanadia (V2O5) loaded on Si-doped TiO2 was obtained by an impregnation method. The mole ratio of Si/Ti was 0.2, NOx conversion exceeds 94% at 300 degrees C and GHSV of 41,324 hr(-1), which is about 20% higher than pure V2O5/TiO2. The catalysts were characterized by XRD, BET, TEM, FT-IR, NH3-TPD, XPS, H...

Graphene-decorated V2O5 nanobelts (GVNBs) were synthesized via a low-temperature hydrothermal method in a single step. V2O5 nanobelts (VNBs) were formed in the presence of graphene oxide, a mild oxidant, which also enhanced the conductivity of GVNBs. From the electron energy loss spectroscopy analysis, the reduced graphene oxide (rGO) are inserted into the layered crystal structure of V2O5 nano...

Bulk quantities of electrically conducting nanotubes of polypyrrole having narrow pore diameter (6 nm) can be synthesized rapidly by chemical oxidative polymerization of pyrrole in the presence of stoichiometric amounts of V2O5 nanofibers. The V2O5 nanofibers act as templates for polymerization and yield, as the initial product, polypyrrole nanotubes with pores filled with V2O5. The V2O5 dissol...

Transition metal oxides and graphene composites have been widely reported in energy storage and conversion systems. However, the controllable synthesis of graphene-based nanocomposites with tunable morphologies is far less reported. In this work, we report the fabrication of V2O5 and reduced graphene oxide composites with nanosheet or nanoparticle-assembled subunits by adjusting the solvotherma...