Fatigue crack growth has been observed recently in ferroelectrics under cyclic electric loading[ Does the crack grow by electric breakdown\ or by the stress _eld near the crack tip< The present paper provides a mechanistic explanation for the electric!_eld!induced fatigue crack growth[ The non!uniform electric _eld near an insulated crack tip might cause domain switching which in turn produces ...

Fatigue crack initiation and early short crack propagation behaviour in two microstructural variants of a recently developed Low Solvus, High Refractory (LSHR) disc superalloy at room temperature has been investigated by three-point bending with replication procedure. The results shows that fine gained (FG) LSHR possesses higher fatigue life due to its better crack initiation resistance, limite...

Finite element simulations are carried out to characterize a new fracture specimen, consisting of an outer circular epoxy ring bonded to an inner circular invar plate for accelerated thermal fatigue testing. Radial cracks are introduced in the epoxy ring. The growth of these radial cracks is correlated to the applied energy release rate G. We studied the dependence of G on the crack length, the...

The use of microwave technique has proved to be a viable means for crack detection and sizing surface cracks in metals. In this technique, the surface of the specimen is interrogated with a radiating open-ended waveguide probe and a crack is assumed to be a simple short-circuited rectangular waveguide, causing peturbations in the probe reflection coefficient. Since the growth of fatigue in meta...

Fatigue crack growth is examined in P/M 2124 aluminum alloys reinforced with SiC particles (SiCp) and whiskers (SiCw) over a wide spectrum of growth rates from 10 to 10 m per cycle. Effects of aging treatment, orientation of crack growth direction with respect to the rolling direction, mean stress (or stress ratio), and reinforcement volume percent on the fatigue crack growth threshold are inve...

The purpose of this study is to discuss the impact fatigue failure mechanism of a suction valve that involves the fracture with fragments torn off from the edge or surface. The shape and dimensions of the test specimen and stopper were made the same as those of the suction valve and stopper in an actual compressor. The specimen was operated by short-duration compressed air pulses, and struck ag...

16 This paper presents a novel large-area strain sensing technology for monitoring fatigue cracks in 17 steel bridges. The technology is based on a soft elastomeric capacitor (SEC), which serves as a 18 flexible and large-area strain gauge. Previous experiments have verified the SEC’s capability to 19 monitor low-cycle fatigue cracks experiencing large plastic deformation and large crack openin...

A study has been made of the fatigue-crack propagation properties of a series of laminated Nbreinforced Nb3Al intermetallic-matrix composites with varying microstructural scale but nominally identical reinforcement volume fraction (20 pct Nb). It was found that resistance to fatigue-crack growth improved with increasing metallic layer thickness (in the range 50 to 250 mm) both in the crack-divi...

Interest in extending the high cycle fatigue life of structures has increased in the last decade of the 20th century. Since a long fatigue life depends on keeping cyclic loads near or below the fatigue threshold, understanding near-threshold behavior is now all the more important. This paper reviews the status of the ‘threshold of fatigue’ and to a lesser extent its relation to the ‘fatigue lim...

Although the propagation of fatigue cracks has been recognized as a problem of clinical significance in dentin, there have been few fracture mechanics-based studies that have investigated this issue. In the present study, in vitro cyclic fatigue experiments were conducted over a range of cyclic frequencies (1-50 Hz) on elephant dentin in order to quantify fatigue-crack growth behavior from the ...