Phosphorene, also known as monolayer black phosphorous, has been widely used in electronic devices due to its superior electrical properties. However, its relatively low Young's modulus, low fracture strength and susceptibility to structural failure has limited its application in nano devices. Therefore, in order to design more mechanically reliable devices that utilize phosphorene, it is neces...

silver nano-particles have different biological applications due to their compatibility. chemical methodsusually result in remaining some amounts of toxic reactions on the nano-particles. for this reason, the useof plants as sustainable and accessible resources in preparation of compatible nano-particles has attracteda lot of attention in the recent years. this research investigated the green s...

objective: bioactive glass 45s5 is a surface reactive glass-ceramic biomaterial, developed in 1969. bag 45s5 with particle size of 20-60 nm has the ability of bone regeneration, broad spectrum antibacterial effect, repairs and replaces diseased or damaged bone. the aim of this study was to evaluate the antibacterial activity and determine mic and mbc values of nano-bag45s5 on streptococcus muta...

Recent experiments on vesicles formed from block copolymers with liquid-crystalline side chains reveal a rich variety of vesicle morphologies. The additional internal order ("structure") developed by these self-assembled block copolymer vesicles can lead to significantly deformed vesicles as a result of the delicate interplay between two-dimensional ordering and vesicle shape. The inevitable to...

Single crystals in nature often demonstrate fascinating intricate porous morphologies rather than classical faceted surfaces. We attempt to grow such crystals, drawing inspiration from biogenic porous single crystals. Here we show that nanoporous single crystals of gold can be grown with no need for any elaborate fabrication steps. These crystals are found to grow following solidification of a ...

Hot-wire chemical vapour deposition (HWCVD) has been used to prepare both hydrogenated amorphous silicon (a-Si:H) and nano/ microcrystalline thin layers as intrinsic material at different deposition conditions, in order to establish optimum conditions where the hydrogen content would be minimal and the films would still exhibit good optical properties. Experimental data shows that by varying de...

We report on the thermally induced changes of the nano-structural and optical properties of hydrogenated nanocrystalline silicon in the temperature range 200-700 degrees C. The as-deposited sample has a high crystalline volume fraction of 53% with an average crystallite size of ~3.9 nm, where 66% of the total hydrogen is bonded as identical withSi-H monohydrides on the nano-crystallite surface....

Synthesis and characterization of nano-crystalline silicon grown by atom beam sputtering technique are reported. Rapid thermal annealing of the deposited films is carried out in Ar + 5% H2 atmosphere for 5 min at different temperatures for precipitation of silicon nano-crystals. The samples are characterized for their optical and structural properties using various techniques. Structural studie...

Nano-structured crystalline tungsten(vi) oxides (WO(3)) were prepared using a colloidal crystal template method; these materials have increased specific surface area compared to crystalline WO(3) prepared without the template, and after platinum loading they show enhanced photocatalytic activity for acetic acid decomposition under visible light.

polyamide-66(pa66)/caco3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. nano-size of caco3 was synthesized by micro-emulsion technique. the material was characterized by xrd, sem, ftir and uv-vis techniques. xrd results of composites suggested that caco3 particles are found in the amorphous phase of the semi-crystallin...