The complete structure of MgSeO4·9H2O has been refined from neutron single-crystal diffraction data obtained at 5, 100, 175 and 250 K. It is monoclinic, space group P2₁/c, Z = 4, with unit-cell parameters a = 7.222 (2), b = 10.484 (3), c = 17.327 (4) Å, β = 109.57 (2)°, and V = 1236.1 (6) Å(3) [ρ(calc) = 1770 (1) kg m(-3)] at 5 K. The structure consists of isolated [Mg(H2O)6](2+) octahedra, [Se...

Magnesium-substituted fluorapatite powders were synthesized by hydrothermal method, and their sintering behavior was investigated by dilatometry in the temperature range 25-1100°C. Analysis of the obtained powders by X-ray diffraction and (31)P NMR spectroscopy showed that the powders consisted of a single apatite phase and no amorphous phase has been formed. Compared to pure fluorapatite, the ...

Mesoporous  MgO  microstructures  were  synthesized  using magnesium  acetate  tetrahydrate,  ammonium  oxalate  monohydrate and  Pluronic  F127  via  heating  at  40  °C  for  24  h  and  subsequent calcination. The mesoporous structure of magnesium oxide with the specific  surface  area  of  47m2 /g,  pore  volume  0.30  cm3 /g  and  the average pore size 24 nm is produced. According to ...

Magnesium is potentially useful for orthopedic and cardiovascular applications. Magnesium and its alloys are light, biodegradable, biocompatible metals that have promising applications as biomaterials. However, the corrosion rate of this metal is so high that its degradation occurs before the end of the healing process. One of the ways to improve the corrosion rate is to compose it with ceramic...

Magnesium is potentially useful for orthopedic and cardiovascular applications. Magnesium and its alloys are light, biodegradable, biocompatible metals that have promising applications as biomaterials. However, the corrosion rate of this metal is so high that its degradation occurs before the end of the healing process. One of the ways to improve the corrosion rate is to compose it with ceramic...

magnesium hydroxide mg(oh)2 nanorods with diameters of 90±10nm and lengths of more than 2μms were prepared by a simple route at ~75oc in ambient air. the approach is based on reaction of magnesium powder and de-ionized water without the use of any harmful, toxic or corrosive reagents. characterization using x-ray diffraction (xrd) shows single crystalline structure of mg(oh)2 (brucite) whereas ...

In this study, Boron carbide was synthesized using Mesoporous Carbon CMK-1, Boron oxide, and magnesiothermic reduction process. The Effects of temperature and magnesium grain size on the formation of boron carbide were studied using nano composite precurser containg mesoporous carbon. Samples were leached in 2M Hydrochloric acid to separate Mg, MgO and magnesium-borat phases. SEM, XRD and Xray ...

To develop an effective process for tantalum powder production, a new preform reduction process (PRP) based on the magnesiothermic reduction of feed preform containing tantalum oxide (Ta2O5) was investigated. The feed preformwas fabricated from slurry, which was made by mixing Ta2O5 powder, flux (e.g., CaCl2), and binder. Various compositions of preform in the form of plates were prepared using...

Sodium picosulfate/magnesium citrate (SPMC) is a widely used oral bowel cleansing agent considered to be relatively safe. However, partially dissolved or undissolved SPMC powder may cause severe injuries of the esophagus and stomach. We report a very rare case of acute gastric injury without esophageal damage caused by the ingestion of undissolved SPMC powder. A 69-year-old man experienced epig...