In the present study, an ultrafine grained (UFG) 304L stainless steel with the average grain size of 300 nm was produced by a combination of cold rolling and annealing. Weldability of the UFG sample was studied by Nd: YAG laser welding under different welding conditions. Taguchi experimental design was used to optimize the effect of frequency, welding time, laser current and laser pulse duratio...

B. Ahn*, S. R. Nutt 1. Department of Chemical Engineering and Materials Science, University of Southern California, Los Angeles, CA, 90089-0241, USA *[email protected] Abstract: Al–Mg alloy powder was mechanically milled in liquid N2 (cryomilling) to produce thermally stable powder with nanocrystalline (NC) microstructure for the manufacture of highstrength alloys. A multi-scale microstructure w...

Nanoindentation morphologies of crystalline copper have been probed at the grain scale. Experimental tests have been conducted on nanocrystalline (NC), ultrafine-grained (UFG), and coarse-grained (CG) copper samples with a new Berkvoich indenter at the strain rate of 0.04/s without holding time at an indentation depth of 2000 nm at room temperature. As the grain size increases, the height of th...

We present the results of in-situ studies of evolution of grain boundary misorientations in ultrafine grained (UFG) aluminum alloy Al-4 Cu-0.5 Zr (wt%) during annealing. The structure of the UFG alloy was obtained by severe plastic deformation method. Misorientations between the grains were measured using single reflection technique. It was found that relaxation processes during annealing are a...

Ultrafine-grained (UFG) nanostructured materials having grain sizes of tens and hundreds of nanometers recently have aroused interest among researchers in the materials science field. With respect to their mechanical properties, one would hope to be able to obtain the extremely strong states that can be expected in the case of strong grain refinement according to the Hall-Petch relationship (Gl...

Al–Mg alloy powder was cryomilled to achieve a nanocrystalline (NC) structure having an average grain size of 50 nm with high thermal stability, and then consolidated by quasi-isostatic forging. The consolidation resulted in a bulk material with ultrafine grains of about 250 nm, and the material exhibited enhanced strength compared to conventionally processed Al–Mg alloy. The hardness of as-cry...

The tensile properties and deformation response of an ultrafine-grained (UFG) Al–Mg alloy with bimodal grain structure were investigated using a micro-straining unit and a strain mapping technique. Atomized Al 5083 powder was ball-milled in liquid N2 to obtain a nanocrystalline (NC) structure, then blended with 50 wt.% unmilled coarse-grained (CG) powder, and consolidated to produce a bimodal g...

The tensile fractures of ultrafine-grained (UFG) Al-Mg alloy with a bimodal grain size were investigated at the microand macroscale using transmission electron microscopy (TEM), scanning electron microscopy (SEM) equipped with focused ion beam (FIB), and optical microscopy. The nanoscale voids and crack behaviors near the tensile fracture surfaces were revealed in various scale ranges and provi...

an ultrafine grained dual phase (ufg dp) steel containing niobium was produced by a new routeutilizing simple cold-rolling and subsequent intercritical annealing of ferrite/martensite duplex startingstructures. the effects of intercritical holding time on the microstructural evolutions and mechanicalproperties were studied. the results showed that increasing intercritical holding time enhnaced ...

Accumulative Roll-Bonding (ARB) is one of the more recently developed techniques capable of producing bulk ultra-fine grained (ufg) metals. There are still many aspects of the behavior of ufg metals that lacks an in-depth understanding, such as a generalized view of the factors that govern the cyclic deformation mechanism(s). This study aims to advance the understanding of the cyclic deformatio...