The aim of this study was to manufacture and test, in vitro, a novel modification to provide fluoride-releasing orthodontic brackets. Thirty-two orthodontic brackets were drilled to produce a recess (approximately 1.3 mm in diameter and 0.7 mm in depth) at the centre of the bracket base. Four materials, with and without the addition of sodium fluoride, a glass ionomer cement (Ketac Cem micro), ...

OBJECTIVE The aim of this study was to investigate how the release of fluoride from two compomers and a fluoridated composite resin was affected by exposure to KF solution. MATERIAL AND METHODS Two compomers (Dyract AP and Compoglass F) and one fluoridated composite (Wave) were prepared as discs (6 mm diameter and 2 mm thick), curing with a standard dental lamp. They were then stored in eithe...

This study evaluated the surface microhardness and fluoride release of 5 restorative materials - Ketac-Fil Plus, Vitremer, Fuji II LC, Freedom and Fluorofil - in two storage media: distilled/deionized water and a pH-cycling (pH 4.6). Twelve specimens of each material, were fabricated and the initial surface microhardness (ISM) was determined in a Shimadzu HMV-2000 microhardness tester (static l...

The aim of this study was to test the null hypothesis that there is no difference in fluoride release between resin-modified glass ionomer cements (RMGICs) and composites in the long term. The materials were divided into 5 groups: a nonfluoride-releasing composite - Group TXT (Transbond XT), a fluoride-releasing composite - Group QC (Quick-Cure), and three RMGICs - Groups FOLC, FOB and MC (Fuji...

OBJECTIVES Fluoride release/recharge properties of fissure sealants are important for their long-term inhibition of caries. This study was conducted to examine the relationship between fluoride release and recharge of pit-and-fissure sealants. METHODS Specimens were prepared from 5 different sealant materials: Fissurit F, a conventional resin; Fuji VII, a glass-ionomer cement (GIC); Fuji II L...

The purposes of this in vivo study were to determine if placing a sealant over a glass ionomer restoration modifies its fluoride release, and to examine the effect on glass ionomer of a 4-min application of topical fluoride. Fluoride release from glass ionomer preventive resin restorations placed in 21 bovine teeth was measured before and after removing their sealants. Fuji II, Ketac Silver, an...

OBJECTIVE This study was designed to evaluate the effect of two bleaching agents on the fluoride release of three types of glass ionomer materials. MATERIALS AND METHODS A total of 90 specimens of the tested materials (Ketac Fil, Photac Fil and F2000) were prepared by a split Teflon ring with an internal diameter of 5 mm and thickness of 2 mm. The tested materials were applied and bleached ac...

The effect of brushing with two abrasive levels on the fluoride release of high-viscosity glass ionomers (GIs) was investigated. Forty-eight GI discs were fabricated and randomly assigned to one of the four groups. Treatments, performed for 30 days, included exposure to a carboxymethylcellulose (CMC) solution without fluoride (CMC-F), CMC with 275 ppm fluoride (CMC+F), CMC with fluoride plus br...

BACKGROUND In the mid of 1980s, the cariostatic effect of fluoride ions on enamel caries had been demonstrated in many studies. The use of fluoride releasing dental restorative materials has seen increasing from many years for the specific purpose of leaching of fluoride into the surrounding tissues to inhibit secondary dental caries as well as prevention of caries in the newly erupted tooth. I...

Glass ionomer cements reportedly bond to tooth surfaces by physicochemical interaction and slowly release fluoride. 1 Two mechanisms are involved in fluoride release, a rapid surface elution and a slower bulk diffusion of fluoride ions. 2, 3 The greatest release of fluoride reportedly occurs in the first 24 hr, and then remains constant for several months before it tapers off after 2 years.4, 5...