Compositionally graded glass-filled epoxy sheets with edge cracks initially along the gradient are studied under dynamic loading conditions. Specimens with monotonically varying volume fraction of reinforcement are subjected to mixed-mode loading by eccentric impact relative to the crack plane. The optical method of Coherent Gradient Sensing and high-speed photography are used to map transient ...

Microstructural degradation is a predominant source of damage in polycrystalline alloys that are commonly used in diverse applications. For early diagnosis and prognosis of failures, it is essential to understand the mechanisms of damage growth specifically in the crack initiation phase, which is still an intriguing phenomenon for scientists due to sensing inaccuracies and modeling uncertaintie...

analytical detection of cracking in connections of steel moment resisting frames using simple damage indices is important since these cracks are not visible unless the connections are uncovered. in this paper, applicability of three cumulative damage indices for detection of cracking in a cover plate welded moment connection is investigated. the damage indices considered in this study are based...

Two distinct mechanisms of crack initiation and advance by void growth have been identified in the literature on the mechanics of ductile fracture. One is the interaction a single void with the crack tip characterizing initiation and the subsequent void by void advance of the tip. This mechanism is represented by the early model of Rice and Johnson and the subsequent more detailed numerical com...

Plate impact experiments are conducted to study the dynamic fracture processes in 4340 VAR steel which occur on submicrosecond timescales. These experiments involve the plane strain loading of a planar crack by a plane tensile pulse with a duration of approximately 1 /xs. The loading is achieved by impacting a precracked, disk-shaped specimen by a thin flyer plate. Motion of the rear surface of...

In all-ceramic restorations, crack formation and propagation phenomena are of major concern, since they may result in intra-oral fracture. The objective of this study was calculation of damage in porcelain MOD inlays by utilization of a finite-element (FE) implementation of the distributed crack theory. "Damage" is defined as the parameter that describes the local decrease of stiffness caused b...

Increasing use of aluminum shape castings in automotive and aerospace industries has drawn great attention to fatigue properties of cast aluminum components. The fatigue resistance of aluminum castings strongly depends upon the presence of casting flaws and characteristics of microstructural constituents. The existence of casting flaws significantly reduces fatigue crack initiation life. In the...

In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of ...

The fundamentals associated with acoustic emission monitoring of fatigue crack initiation and propagation of Ti-6AI-4V were studied. Acoustic emission can detect and locate incipient fatigue crack extensions of approximately 1 0 gm. The technique therefore can serve as a sensitive warning to material failure. There are three distinct stages during which acoustic emission is generated. These sta...

The modulus and internal friction of Armco iron rere continuously measured during cathodic charging rith hydtogen to investigate crack initiation and grorth. The observed modulus decrease ras attributed to crack initiation and grorth. The internal friction increase doring cathodic charging ras atfributed to plastic deformation accompanying the crack formation. Both the modulos and internal fric...