The 316L stainless steel has been widely used in both artificial knee and hip joints in biomedical applications. The average lifetime of artificial hip joints is about 10 years due to aseptic loosening of the femoral stem attributed to polymeric wear debris; however, there is a steadily increasing demand from younger osteoarthritis patients aged between 15 and 40 years for a longer lasting join...

The study comprises evaluation of suitability of passive layer created on the surface of AISI 316L stainless steel for products that are intended to have contact with blood. For that purpose, prior to and after chemical passivation, samples were subject to 7 day exposure in artificial plasma at the temperature of T=37°C. Next, tests of metallic ions infiltration from the surface to the solution...

In modern history, metals have been used as implants since more than 100 years ago when Lane first introduced metal plate for bone fracture fixation in 1895 (Lane, 1895). In the early development, metal implants faced corrosion and insufficient strength problems (Lambotte, 1909, Sherman, 1912). Shortly after the introduction of the 18-8 stainless steel in 1920s, which has had far-superior corro...

In this study, the synergistic effects of abrasion and corrosion on AISI 316L stainless steel have been investigated using a micro-abrasion test rig. A series of results from abrasioncorrosion tests conducted using the micro-abrasion rig are presented. AISI 316L stainless steel has been studied under both pure abrasion and abrasion-corrosion conditions simulated by either distilled water or 3.5...

A stent in artery is subjected to significant mechanical loads due to the repetitive cyclical pressure loads and displacement of the artery wall. The arteries expands and contracts slightly as the pressure changes with the heart beat for long-term in-vivo service. The structure of the stent has to withstand these loads while scaffolding the narrow artery. Many different stent designs and materi...

A simple and effective method without vacuum to control the wetting properties of AISI 316L stainless steel using femtosecond laser pulses at high repetition rate has been developed. Both hydrophilic and hydrophobic surfaces were formed by creating micro-conical structures on the surface with femtosecond laser irradiation in air. The scan speed was found to be an effective parameter in controll...

The purpose of the tests was to determine whether and how sterilisation process of samples made of AISI 316L stainless steel with diff erent strain impacts their corrosion resistance. Tests were made on steel samples that had been electrochemically polished in order to assure proper surface roughness. In order to evaluate the infl uence of sterilisation on physical and chemical properties of st...

INTRODUCTION: Cannulated screws, along with guide wires, are commonly used for a variety of orthopedic indications. Typically they are used for fractures in cancellous regions. Breakage or bending deformation of the guide wire is a clinical concern. Therefore it would be advantageous to use Co-Cr alloys such as MP35N and L605 in these applications as the occurrence of breakages and bendings wou...

The corrosion behaviour of 316L stainless steel coatings obtained by cold spray method was investigated in this study. 316L powders were deposited onto Al5052 aluminum substrates. The coatings were produced using nitrogen (N2) process gas. In order to further improve the corrosion and mechanical properties of the coatings, heat treatment was applied at 250 and 750 °C. The corrosion performances...

Wear of Poly (Methyl MethAcrylate), PMMA, against a metallic surface, AISI 316L stainless steel, SS, has been investigated in dry conditions. These materials have been used to simulate the degradation of the contact, femoral stem-bone cement in the field of hip prosthesis. First of all, no significant wear was observed on the 316L SS. PMMA wear has been quantified: the energy wear coefficient, ...