aisi 304l austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensiticprocess. corrosion behavior of different samples was investigated in a 0.5m hcl solution using open circuitpotential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. also, the correlationbetween the grain size and pitting corrosion resistance was asses...

In this paper, an advanced thermo-mechanical treatment was conducted on AISI 316 austenitic stainless steel. At first, three samples were rolled at the ambient temperature, the temperature of -20 ºC (dry ice and ethanol) and -196 ºC (liquid nitrogen). Then, the samples were annealed at 800 ºC in the time range of 1 to 15 minutes. In each step, the microhardness values of the samples were measur...

To provide insight into the relationships between precipitation phenomena, grain size and mechanical behavior in a complex precipitation-strengthened alloy system, Al 7075 alloy, a commonly used aluminum alloy, was selected as a model system in the present study. Ultrafine-grained (UFG) bulk materials were fabricated through cryomilling, degassing, hot isostatic pressing and extrusion, followed...

The work is devoted to the study of corrosion behavior TiNi alloys with original austenitic and martensitic structure in various states. In course research, it was found that rate destruction for coarse-grained ultrafine-grained Ti 49.0 Ni 51.0 different: alloy turned out be less resistant higher than state. X-ray phase analysis revealed as a result processes, change composition occurs, accompa...

We have investigated the effects of helium ion irradiation energy and sample temperature on the performance of grain boundaries as helium sinks in ultrafine grained and nanocrystalline tungsten. Irradiations were performed at displacement and non-displacement energies and at temperatures above and below that required for vacancy migration. Microstructural investigations were performed using Tra...