Fatigue crack propagation tests under high–low and low–high block loading sequences have been performed in aluminium alloy specimens. The tests were carried out at constant DK conditions. Two stress ratios were analysed: R = 0.05 and R = 0.4. Crack closure was monitored in all tests by the compliance technique using a pin microgauge. The observed transient post load step behaviour is discussed ...

A major part of fracture mechanics is concerned with studying the initiation and propagation of fatigue cracks. This typically requires constant monitoring of crack growth during fatigue cycles and the knowledge of the precise location of the crack tip at any given time. One technique currently available for measuring fatigue crack length is the Potential Drop method[1]. The method, however, ma...

In-phase TMF crack growth testing with different lengths of the hold time at the maximum temperature of 550C has been conducted on Inconel 718 specimens. Focus has been on establishing a method for TMF crack growth testing and investigating the effect of high temperature hold times on the TMF crack growth of the material. The tests are compared to isothermal crack propagation tests and show go...

Recent theoretical results on elastic-plastic planestrain crack growth an~ reviewed and experimental results for crack growth in a 4140 steel are discussed in terms of the theoretical concepts. The theory is based on a recent asymptotic analysis of crack surface opening and strain distributions at a quasistatically advancing crack tip in an ideally plastic solid. The analysis is incomplete in t...

The present paper is concerned with the application of a “plasticity-induced” crack closure model to study fatigue crack growth under various load histories. The model was based on the Dugdale model but modified to leave plastically deformed material in the wake of the advancing crack. The model was used to correlate crack growth rates under constant-amplitude loading and then used to predict c...

The vibration behavior of an atomic force microscope [AFM] cantilever with a crack during the nanomachining process is studied. The cantilever is divided into two segments by the crack, and a rotational spring is used to simulate the crack. The two individual governing equations of transverse vibration for the cracked cantilever can be expressed. However, the corresponding boundary conditions a...

Engineering problems shunned previously rise to the surface gradually with the activities of reforming the natural world in depth, the problem of expansive soil crack under the changing environment becoming a control factor of expansive soil slope stability. The problem of expansive soil crack has gradually become a research hotspot, elaborates the occurrence and development of cracks from the ...

Abstract. Due to their microstructure, quasi brittle materials present rough cracks. Under sliding of the crack lips, this roughness involves in one hand induced opening and in the other hand some apparent plasticity which is due to the interlocking of the crack lips combined with Coulomb’s friction. The proposed model is written under the irreversible thermodynamics framework. Micromechanics u...

Prognostics and health management techniques have drawn widespread attention due to their ability to facilitate maintenance activities based on need. On-line prognosis of fatigue crack propagation can offer information for optimizing operation and maintenance strategies in real-time. This paper proposes a Lamb wave-particle filter (LW-PF)-based method for on-line prognosis of fatigue crack prop...

A major part of fracture mechanics is concerned with studying the initiation and propagation of fatigue cracks. This typically requires constant monitoring of crack growth during fatigue cycles which necessitates automation of the whole process. If the rate of crack growth can be determined the experimenter can vary externally controlled parameters such as load level, load cycle frequency and s...