The causes and the prevention of carbon steel corrosion in amine systems are reviewed. The corrosive agents are acid gases, oxygen, heat stable salts, amine degradation products, and, in refineries, gas contaminants such as ammonia and hydrogen cyanide. Corrosion mechanisms are provided for carbon steel exposed to amine solutions and for amine regenerator overhead systems containing aqueous con...

Cyclic Potentiodynamic polarization studies were conducted to compare the corrosion resistance of Nitinol cardiovascular stents and stainless steel stents. The tests is to simulate the corrosion behavior of the stents under body condition using Phosphate Buffered Saline (PBS) solution at 37C and following the ASTM F2129-01, Item 2, WK1749, Standard. The results of this study indicate that both ...

A corrosion inhibitor is a chemical substance which, when added in small concentrations to an environment, minimizes or prevents corrosion [I]. Corrosion inhibitors are used to protect metals from corrosion, including temporary protection during storage or transport as well as localized protection, required, for example, to prevent corrosion that may result from accumulation of small amounts of...

ball mills are common grinding equipment in mineral processing industries. ball wear results from three mechanisms namely impact, abrasion and corrosion. of these, the corrosion mechanism is the least investigated, due to its chemical-electrochemical nature. therefore, the aims of this research were to investigate the grinding chemistry influence (slurry ph, solid percentage, water chemistry an...

Reinforced concrete beams are normally designed as under-reinforced to provide ductile behaviour at failure i.e. the tensile moment of resistance, Mt(0), is less than the moment of resistance of the compressive zone, Mc. Since it is well established that the steel in reinforced concrete beams is prone to corrosion, the residual flexural strength is normally the main concern of asset managers. H...

The high-velocity oxygen-fuel (HVOF) spraying process was used to fabricate conventional WC-10Co-4Cr coatings and FeCrSiBMn amorphous/nanocrystalline coatings. The synergistic effect of cavitation erosion and corrosion of both coatings was investigated. The results showed that the WC-10Co-4Cr coating had better cavitation erosion-corrosion resistance than the FeCrSiBMn coating in 3.5 wt.% NaCl ...

Corrosion behavior of solution annealed high-carbon and low-carbon CoCrMo wrought alloy, commonly used in medical joint implants, was investigated. The surface passivation properties remained similar with and without the various solution anneal conditions, while the rate of corrosion was lower for solution annealed high-carbon CoCrMo. Corrosion was found to target phase boundaries and certain g...

This paper discusses chemical and galvanic corrosion of tungsten nitride carbide (WNC) barrier metal. Chemical corrosion occurs due to the oxidation of W in the WNC film by H2O2, which is used as oxidizer in CMP slurries, followed by the dissolution of the oxide complex. Galvanic corrosion takes place due to the high potential difference between Cu and WNC established in the presence of H2O2 ba...

A time–frequency analysis-based signal processing study for detecting active corrosion in aluminum plate-like structure utilizing the broadband piezoelectric wafer active sensors is presented in this article. Tests were conducted on an aluminum plate with a network of sensors installed on one side of the plate for Lamb wave generation and reception. The corrosion was emulated as material loss o...

Corrosion is a relatively slow material degradation process to which metallic structures of aircraft are subjected during service and it can appear in many forms. Generally, corrosion protection for preventing or inhibiting the formation and growth of corrosion damage on aircraft structures is well-established technology. Unfortunately, despite preventive measures, corrosion does occur and its ...