Vanillin is an interesting corrosion inhibitor because of its safe use and high solubility inwater. The effect of vanillin on the corrosion inhibition of carbon steel in 1.0 Mhydrochloric acid solution has been studied using potentiodynamic polarization,electrochemical impedance spectroscopy (EIS) and electrochemical noise (EN) techniques.The effect of temperature on the rate of corrosion in th...

The conclusions of an experimental program involving altered tensile strength and microstructure of stainless compressor valve steel are described. The paper presents the results of measurements of ductility, corrosion resistance, bending fatigue strength and damping. Encouraging indications have been achieved concerning the possibilities to further improve the characteristics of current materi...

Corrosion simply refers to destructive and unintentional attack on metals. It is extractive metallurgy in reverse. That is, it serves to return metals back to their ores.1 Corrosion has been recognized as a phenomenon that has existed for as long as mankind. It has devastated several plants in the industrial age, bringing into focus the need to study and understand it. Since then, mankind has c...

The inhibition efficiency (IE) of an aqueous extract of beet root (BR) in controlling corrosion of carbon steel in well water in the absence and presence of Zn 2+ has been evaluated by mass loss method. The formulation consisting of 4 mL of BR extract and 50 ppm Zn 2+ offers 98% inhibition efficiency to carbon steel immersed in well water. A synergistic effect exists between BR extract and Zn 2...

Reinforced concrete beams are normally designed as under-reinforced to provide ductile behaviour at failure i.e. the tensile moment of resistance, Mt(0), is less than the moment of resistance of the compressive zone, Mc. Since it is well established that the steel in reinforced concrete beams is prone to corrosion, the residual flexural strength is normally the main concern of asset managers. H...

The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...

In recent decades, the application of fibre-reinforced polymer (FRP) composites for strengthening structural elements has become an efficient option to meet the increased cyclic loads or repair due to corrosion or fatigue cracking. Hence, the objective of this study is to explore the existing FRP reinforcing techniques to care for fatigue damaged structural steel elements. This study covers the...

An arc-sprayed amorphous Al–Ti–Ni coating on S355 structural steel was processed by laser remelting (LR) at powers of 600, 800, and 1000 W. The surface-cross-sectional morphologies, chemical element distributions, and phase compositions of the as-obtained Al–Ti–Ni coatings were analyzed using a scanning electron microscope (SEM), energy-dispersive spectrometer (EDS), and X-ray diffractometer (X...

The inhibition for the corrosion of mild steel in sulphuric acid solution by the extract of Stevia rebaudiana leaves has been studied using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques. Inhibition was found to increase with increasing concentration of the leaves extract. The effect of temperature on the corrosion behavior of mild steel in 0.5M H2SO4 w...