Ultra-thin graphene coating has been reported to provide considerable resistance against corrosion during short-term exposures, however, there is great variability in the corrosion resistance due to graphene coating in different studies. It may be possible to overcome the problem of hampered corrosion protection ability of graphene that is caused due to defective single layer graphene by applyi...

The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...

The corrosion behavior of pure Fe under a Na₂SO₄ deposit in an atmosphere of O₂ + H₂O was investigated at 500 °C by thermo gravimetric, and electrochemical measurements, viz. potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and surface characterization methods viz. X-ray diffraction (XRD), and scanning electron microscope (SEM)/energy dispersive spectroscopy(EDS). The...

The corrosion of dental biomaterials is a pertinent clinical issue. In spite of the recent innovative metallurgical and technological advances and remarkable progress in the design and development of surgical and dental materials, failures do occur. The present article describes the problem of corrosion in titanium dental implants. The clinical significance of the dental implant corrosion is hi...

Aluminum based metal matrix composites (MMCs) have received considerable attention in the automotive, aerospace and nuclear industries. One of the main challenges using Al-based MMCs is the influence of the reinforcement particles on the corrosion resistance. In the present study, the corrosion behavior of Al-B₄C MMCs in a 3.5 wt.% NaCl solution were investigated using potentiodynamic polarizat...

In vivo degradation predication faces a huge challenge via in vitro corrosion test due to the difficulty for mimicking the complicated microenvironment with various influencing factors. A thin electrolyte layer (TEL) cell for in vitro corrosion of pure magnesium and AZ91 alloy was presented to stimulate the in vivo corrosion in the micro-environment built by the interface of the implant and its...

The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O2 flow at 600 ̋C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and...

In this study a numerical model is developed to predict the effects of corrosion on the mechanical integrity of bioabsorbable metallic stents. To calibrate the model, the effects of corrosion on the integrity of biodegradable metallic foils are assessed experimentally. In addition, the effects of mechanical loading on the corrosion behaviour of the foil samples are determined. A phenomenologica...

Microbiologically influenced corrosion is responsible for most of the internal corrosion problems in oil transportation pipelines and storage tanks. One problematic area in treating gas lines is the occurrence of the stratification of water in the line. Under these conditions, corrosion inhibitors do not come into contact properly and oil and inhibitors undergo degradation. The role of bacteria...

Corrosion at the head-neck taper has been recently identified as a cause of adverse local tissue reaction. There are no guidelines concerning removal of fixed femoral components when corrosion is present. The objective of this study is to report the survivorship when a new metal ball is placed on a corroded stem. We examined 86 retrieved femoral heads from metal-on-polyethylene THAs that underw...