this work describes the optical and structure properties of nickel sulfide and cobalt sulfide nanoparticles in zsm-5 zeolite. the samples were obtained by sulfidation of the ni2+ and co2+ ion-exchange zsm-5 zeolites in a na2s solution at room temperature. the optical properties of the samples were studied by uv-visible spectroscopy. their crystalline structure and morphology were studied by x-r...

This study developed an upgrading process focusing on acid transformations of water phase pyrolysis bio-oils to esters of oxygen-containing fuels via ZSM−5 catalyst. Temperature was set as a factor with five levels ranging from 60 to 135 °C with reaction time from 1 to 8 h. The results showed that 89% of high acid conversion and over 90% of ester selectivity was obtained from the feedstock via ...

Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AIPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was foun...

The purpose of this work is to develop a low-cost and high-performance catalyst for the selective catalytic hydrogenation acetylene ethylene. Non-precious metals Cu Ni were selected as active ingredients study. Using ZSM-12 carrier, Cu-Ni bimetallic catalysts CuNix/ZSM-12 (x = 5, 7, 9, 11) with different Ni/Cu ratios prepared by incipient wetness impregnation method. total loading 2 wt%. Under ...

LaMnO3 and LaMnO3/ZSM-5 nano catalysts were synthesized by Pechini method and their physical-chemical properties were characterized using XRD, FTIR, SEM-EDX, UV-vis DRS, BET surface area and TPR. The correlation between characteristic properties and activity of catalysts were investigated. The catalytic performance of the catalysts was evaluated in combustion of 2-propanol...

Vanadium silicates such as V-Al-analcime, V-analcime, V-magediite and V-ZSM-11 were synthesized using vanadium pentoxide or vanadyl sulfates. Vanadium silicates with analcime structure with and without aluminum (V-Al-analcime, V-analcime) were prepared as pure phase by hydrothermal crystallization from a gel with molar composition of (1 SiO2; 0.2 V2O5; 1 Na2O; 0.034 Al2O3; 35.7 H2O) and (1 SiO2...

Zeolites have been successfully applied as catalysts in the pyrolysis of plastics to obtain valuable lower molecular weight hydrocarbon compounds. In present work, mordenite was directly synthesized and chemically modified from commercial increase pore volume. For first time, performance these mordenites compared with that an alkali-treated ZSM-5 for assisting simulated urban plastic waste. The...

The use of H-ZSM-5 with various binders (Al 2 O 3 , SiO and kaolinite, 10 wt% on catalyst formulation) for the catalytic conversion glycerol to bio-based aromatics (GTA) was investigated in a continuous bench-scale unit at pyrolysis temperature 450 °C, upgrading 500 WHSV pure 1 h ?1 atmospheric pressure, their performance compared (SiO /Al molar ratio 28). latter gave peak BTX carbon yield ca. ...

The realization of biofuels and chemicals requires the development highly active selective catalysts, which are resistant to deactivation. A conventional ZSM-5 (SiO2/Al2O3 = 30) was modified with 0.2 M NaOH generate a mesoporous zeolite support. parent zeolite, mic-ZSM-5, hie-ZSM-5, silica support, SiO2, were impregnated 5% nickel characterized using X-ray powder diffraction (XRD), Brunauer–Emm...

A novel modified Ni-ZSM-5 nanozeolite was fabricated via an organic template-free hydrothermal route. The average particle size of Ni-ZSM-5 nanozeolite was calculated to be 85 nm by scanning electronic microscopy. Then, Carbon paste electrode (CPE) was modified by Ni-ZSM-5 nanozeolite and Ni2+ ions were then incorporated to the nanozeolite matrix. Electrochemical behavior of this electrode was ...