The aims of this study were to investigate the effects of Zr addition and potentiodynamic polarization on the microstructure and corrosion resistance of Ti–22Nb and Ti–22Nb–6Zr alloy samples. The corrosion tests were carried out in 0.9% NaCl at 37 8C and neutral pH value, utilizing the OCP, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques.The results of ...

This work offers an analysis of the wire feedability-related properties of Al-5Mg solid wire electrodes bearing Zr. Effects of Zr content on microstructures and mechanical properties of the Al-5Mg alloys were studied. Experimental results have demonstrated that α-Al dendrites of the as-cast Al-5Mg alloy are refined, and the tensile strength, microhardness and roughness of the 1.2 mm wire electr...

The precipitation hardening behavior of an Al-0.08Zr-0.014Sc-0.008Er-0.10Si (at.%) alloy was investigated utilizing microhardness, electrical conductivity, atom-probe tomography (APT), and compressive creepmeasurements. This new composition, with a Sc:Zr atomic ratio of less than 1:5 represents a significant reduction of the alloy's cost when compared to the more usual Al-0.06Sc-0.02Zr based al...

Structures operating at high temperatures and exposed to aggressive gaseous media are made of low-alloy molybdenum TsM-10 of the system Mo-Al-B, TsM-6 of the system Mo-Zr-B and TsM-12 of the system Mo-Zr-Hf-B [1, 2]. Alloy TsM-10 is commercially pure molybdenum deoxidized by aluminium and boron. Alloy TsM-6 is alloyed with up to 0.2 wt. % zirconium and TsM-12, is alloyed with up to 0.03 wt. % z...

The TiCp/Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiCp/Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu-Cr-Zr alloys to fabricate the nano-sized TiCp-reinforced Cu-Cr-Zr composites. Results show that nano-sized TiCp can effectively refine the grain size of Cu-Cr-Zr alloys. The morphologies of grain in Cu-Cr-Zr c...

The goal of this study was to optimize the activation behaviour of hydrogen storage alloy TiFe. We found that the addition of a small amount of Zr in TiFe alloy greatly reduces the hydrogenation activation time. Two different procedural synthesis methods were applied: co-melt, where the TiFe was melted and afterward re-melted with the addition of Zr, and single-melt, where Ti, Fe and Zr were me...

The effect of substituting 0.01 or 0.02 at.% Er for Sc in an Al–0.06 Zr–0.06 Sc at.% alloy was studied to develop cost-effective high-temperature aluminum alloys for aerospace and automotive applications. Spheroidal, coherent, L12-ordered Al3(Sc, Zr, Er) precipitates with a structure consisting of an Er-enriched core surrounded by a Sc-enriched inner shell and a Zr-enriched outer shell (core/do...

It is generally accepted that the electrochemical discharge capacity of a hydrogen storage alloy is closely related to its crystal characteristics. From our experiment, the discharge capacity of AB type Laves phase hydrogen storage alloy ZrCr Mn V Ni 2 0.4 0.2 0.1 1.3 21 21 decreased sharply from 324 mAh g to 25 mAh g after amorphization by mechanically milling the crystalline (as-cast) alloy w...

Metallic alloys are normally composed of multiple constituent elements in order to achieve integration of a plurality of properties required in technological applications. However, conventional alloy development paradigm, by sequential trial-and-error approach, requires completely unrelated strategies to optimize compositions out of a vast phase space, making alloy development time consuming an...

The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructura...