Al~tract--The mechanics of fracture of a stably extending interface crack in polymeric adhesive bonds undergoing very large shear deformation is studied using a rate-del~ndent finite element analysis. Plane-strain and J2 plasticity conditions are considered. Based on recent experimental observations, it is assumed that the local engineering shear strain at a certain distance (i.e. for the polym...

Micro cracks occurring in concrete around tensile rebar is well known latent damage phenomenon. These micro cracks develop, and can be detected after reaching the surface of the concrete. Detection of these cracks before they are fully formed is preferable, but observing the whole crack structure is difficult. Another problem is repairing micro cracks under the concrete surface. The autogenous ...

Cracks can occur in the articular cartilage surface due to the mechanical loading of the synovial joint, trauma or wear and tear. However, the propagation of such cracks under different frequencies of loading is unknown. The objective of this study was to determine the effect of frequency of loading on the growth of a pre-existing crack in cartilage specimens subjected to cyclic tensile strain....

Fatigue is the progressive, localized, permanent structural change that occurs in materials subjected to fluctuating stresses and strains that may result in cracks or fracture after a sufficient number of fluctuations. Fatigue fractures are caused by the simultaneous action of cyclic stress, tensile stress and plastic strain. If any one of these three is not present, fatigue cracking will not i...

Recent observations on the dynamics of crack and fault rupture are described, together with related theory and simulations in the framework of continuum elastodynamics. Topics include con gurational instabilities of tensile crack fronts (crack front waves, disordering, sidebranching), the connection between frictional slip laws and modes of rupture propagation in earth faulting, especially cond...

This paper was to verify the STAGS (general shell, geometric and material nonlinear) code and the critical crack-tip-opening angle (CTOA) fracture criterion for predicting stable tearing in cracked panels that fail with severe out-of-plane buckling. Materials considered ranged from brittle to ductile behavior. Test data used in this study are reported elsewhere. The STAGS code was used to model...

The aim of this study is to evaluate the microstructures, tensile lap shear strength, and fatigue resistance of 6022-T43 aluminum alloy joints welded via a solid-state welding technique-ultrasonic spot welding (USW)-at different energy levels. An ultra-fine necklace-like equiaxed grain structure is observed along the weld line due to the occurrence of dynamic crystallization, with smaller grain...

Vickers indentation fracture can be used to estimate equibiaxial residual stresses (RS) in brittle materials. Previous, conceptually-equal, analytical models were established on the assumptions that (i) the crack be of a semi-circular shape and (ii) that the shape not be affected by RS. A generalized analytical model that accounts for the crack shape and its change is presented. To assess these...

The intrinsic coupling between the mechanical and the electric _elds assigns a unique feature for the fracture in a piezoelectric solid[ We model the kink of a crack by continuous distribution of edge dislocations and electric dipoles[ The problem admits an approach based on the Stroh formalism[ A set of coupled singular integral equations are derived for the dislocation and electric dipole den...

The paper presents a new analytical model to study the evolution of radial cracking around a corroding steel reinforcement bar embedded in concrete. The concrete cover for the corroding rebar is modelled as a thick-walled cylinder subject to axisymmetrical displacement constraint at the internal boundary generated by expansive corrosion products. A bilinear softening curve reflecting realistic ...