A tensile split Hopkinson bar apparatus is developed for testing high strain rate behavior of glass-filled epoxy. The apparatus uses a specimen gripping configuration which does not require fastening and/or gluing and can be readily used for castable materials. Details of the experimental setup, design of grips and specimen, specimen preparation method, benchmark experiments, and tensile respon...

In the published literature there are controversial data to the biomechanical stability of monocortical comparing to the bicortical fixation of metacarpal fractures. The aim of this study was to compare the biomechanical stability of monocortical and bicortical locking osteosynthesis in quasi-static and dynamic 4-point bending tests of composite third metacarpal bone (4th Gen third metacarpal, ...

In this article, an efficient methodology is presented to optimize the topology of structural systems under transient loads. Equivalent static loads concept is used to deal with transient loads and to solve an alternate quasi-static optimization problem. The maximum strain energy of the structure under the transient load during the loading interval is used as objective function. The objective f...

OBJECTIVES The purpose of this in vitro study was to compare the centric and eccentric quasi-static and fatigue fracture strength of industrially prefabricated resin-bonded three-unit inlay-retained fixed dental prostheses (IPIRFDPs). The IPIRFDPs consisted of industrial manufactured yttria-stabilized tetragonal zirconia (Y-TZP) frameworks with an industrially added microhybrid composite veneer...

Although clinical bone fractures occur predominantly under impact loading (as occurs during sporting accidents, falls, high-speed impacts or other catastrophic events), experimentally validated studies on the dynamic fracture behavior of bone, at the loading rates associated with such events, remain limited. In this study, a series of tests were performed on femoral specimens obtained post-mort...

In this paper, progressive damage and global failure of composite laminates under quasi-static, monotonic loading are investigated using 3D continuum damage mechanics. For this purpose, a finite element program has been developed using an eight-node 2D layered element including layer-wise plate theory. Damage analysis of a single orthotropic layer under various uniform in-plane and transverse l...

The indentation deformation and cracking responses of ion-exchanged glasses were measured using quasi-static and dynamic loading cycles. Two glass types were compared, a normal glass that deforms to a large extent by a shearing mechanism and a damage-resistant glass that comparatively deforms with less shear and more densification. The quasi-static indentation cracking threshold for median/radi...

In this article, the 3 point bending analysis of a mobile phone using LS-DYNA explicit integration method is discussed. Since there are a large number of contact pairs defined in the FEA model, and the FEA model is very large in a 3 point bending analysis of a phone, it is much more convenient to use the explicit method than the implicit method. However, using explicit procedure to a quasi-stat...

Rate effects for adhesively-bonded joints in steel sheets failing by mode-I fracture and plastic deformation were examined. Three types of test geometries were used to provide a range of crack velocities between 0.1 mm/s and 5000 mm/s: a DCB geometry under displacement control, a wedge geometry under displacement control, and a wedge geometry loaded under impact conditions. Two fracture modes w...

Strain-rate effects on fracture behavior of unidirectional composite materials are studied. Single-edge notched multi-layered unidirectional graphite composites (T800/3900-2) are investigated to examine fracture responses under static and dynamic loading conditions using a digital speckle correlation method. The fracture parameters for growing cracks are extracted as a function of fiber orienta...