Synthesis and characterization of Cd-TiO2/PEG/FA nanocomposite as a biomaterial is the main aim of this research. Cd-doped TiO2 nanoparticles (NPs) were synthesized by solvothermal assisted sol-gel method. Then, polyethylene glycol (PEG) was added to the as-synthesized NPs in order to modify their surface and to prevent agglomeration. In the next step, folic acid (FA) was conjugated to Cd-TiO2/...

the influences of anionic sodium dodecylsulfate (sds) and cationic hexadecyltrimethylammonium bromide (htab) surfactants on the incorporation and distribution of barium hexaferrite nanoparticles in the electrodeposited cofe-bafe12o19 composite thin films were studied. sulphate bathes with natural ph containing 0 to 2 g/l surfactants were used for electroplating at room temperature. field emissi...

Thousands of tons of macadamia skin waste are generated annually with very limited utilisation of this extensive by-product. The aim of this study was to develop optimal ultrasonic extraction conditions for maximized recovery of phenolic compounds and antioxidant properties from macadamia skin using Response Surface Methodology (RSM). Three ultrasonic parameters, including temperature (30–50 °C...

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...

in recent years many research works have been carried out on anti-corrosive nanocomposites coatings containing mineral reinforcements. the most important criteria in these attempts are polymerization method and the type of matrix and reinforcement of nanocomposites. in this regard, the physical and mechanical properties of the polymers in which a small amount of filler is used can be improved. ...

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels. The mixture was placed under ultrasonic irradiation for 2 hours. After the aging time and filtration of the reaction mixture, the filtrated composite gel was calcinated at 500 °C for 3h in furnace. The precursor gels of zirconium and zinc were prepared ...

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels. The mixture was placed under ultrasonic irradiation for 2 hours. After the aging time and filtration of the reaction mixture, the filtrated composite gel was calcinated at 500 °C for 3h in furnace. The precursor gels of zirconium and zinc were prepared ...

In this paper, ultrasonic irradiation was applied for the synthesis of K2Ti6O13 nanobelts and novel nanocomposite (PbS-CdS/Ti6O13) through ion exchanging and co-intercalation processes. Thirty minutes of ultrasonic irradiation caused the formation of pure, uniform potassium hexatitanate with smaller particle size. The incorporation of PbS and CdS nanoparticles into the layers and on the surface...

Launch vehicles use ablative nozzle liners to function under very high thermal and erosive environments. In solid motor nozzle throats, graphite or carbon phenolic materials are used because of their high heat of ablation and erosion resistance. Ultrasonic testing is implemented as the primary NDT technique for throat insert liners by almost replacing radiography testing. Though introduced for ...