The observation of intense visible fluorescence from silver and iron nanoparticles in different solution phases and surface capping is reported here. Metallic silver and iron nanoparticles were obtained by exploding pure silver and iron wires in pure water. Bovine serum albumin protein adsorption on the silver nanoparticles showed an enhanced fluorescence. The presence of polyvinyl pyrrolidone ...

FePt/iron oxide core/shell nanoparticles are synthesized by a two step polyol process with 1,2hexadecanediol as the reducing reagent. Monodispersed 2.6-nm FePt nanoparticles are first obtained by reduction of iron(III) acetylacetonate and platinum(II) acetylacetonate. These preformed FePt nanoparticles are then used as seeds and an iron oxide shell is formed in the second synthesis step. The ro...

In this study, Fe(II) complexes of phenyldithiocarbamate, dimethyldithiocarbamate and imidazolyldithiocarbamate were used as single-source precursors to prepare iron sulphide nanoparticles by thermolysis in oleic acid/octadecylamine (ODA) at 180 °C. The nanoparticles were dispersed into hydroxyethyl cellulose (HEC) to prepare iron sulphide/HEC nanocomposites. Ultraviolet-Visible (UV-Vis), Photo...

The iron oxide nanoparticles have been synthesized in co-precipitation method using aqueous solution of ferric and ferrous ions with sodium salt. The synthesis of iron-oxide nanoparticles were validated by UV-Visible spectroscopy which showed higher peak at 370 nm as valid standard reference. An average size of iron oxide nanoparticle found by diffraction light scattering (DLS) particle size an...

While nanoparticles exert bactericidal effects through the generation of reactive oxygen species (ROS), the processes of the internalization of and the direct physical damage caused by iron oxide nanoparticles are not completely clear. We hypothesize that direct physical or mechanical damage of the cell membrane and cytoplasmic integrity by nanoparticles is another major cause of bacterial deat...

OBJECTIVES The absorption of commonly used ferrous iron salts from intestinal segments at neutral to slightly alkaline pH is low, mainly because soluble ferrous iron is easily oxidized to poorly soluble ferric iron and ferrous iron but not ferric iron is carried by the divalent metal transporter DMT-1. Moreover, ferrous iron frequently causes gastrointestinal side effects. In iron(III)-hydroxid...

Nanosized iron oxide particles exhibit osteogenic and radiopaque properties. Thus, iron oxide (Fe3O4) nanoparticles were incorporated into a biodegradable polymer (poly-L-lactic acid, PLLA) to fabricate a composite bone screw. This multifunctional, 3D printable bone screw was detectable on X-ray examination. In this study, mechanical tests including three-point bending and ultimate tensile stre...

BACKGROUND Superparamagnetic iron oxide nanoparticles have been used in clinical applications as a diagnostic contrasting agent. Previous studies showed that iron oxide nanoparticles deposited in the liver and spleen after systemic administration. The present study investigated the effect of iron oxide nanoparticles on antigen-specific immune responses in mice sensitized with the T cell-depende...

Here we report a new, bench-top synthesis for iron/iron oxide core/shell nanoparticles via the thermal decomposition of Fe(η(5)-C(6)H(3)Me(4))(2). The iron/iron oxide core/shell nanoparticles are superparamagnetic at room temperature and show improved negative contrast in T(2)-weighted MR imaging compared to pure iron oxides nanoparticles, and have a transverse relaxivity (r(2)) of 332 mM(-1) s...

in this study, magnetic iron oxide nanoparticles (fe3o4) with the size range of 20-30 nm were prepared by the modified controlled chemical co-precipitation method from the solution of ferrous/ferric mixed salt-solution in alkaline medium. in this process polyethylene glycol was used as a surfactant to prevent the solution from agglomeration. the prepared magnetic nanoparticles were characterize...