microalloyed cast steels are a group of microalloyed steels in which reliable mechanical properties could be achieved by heat treatment. in this work, the heat treatment processes were carried out on the cast specimens as the step samples by different thicknesses and zr content. the results show that after homogenization, variations in thickness have no effect on the hardness. also, after hea...

The microstructure of HP stainless steel in aged and aged + solution annealed conditions and solutionized alloy 800 was characterized by optical microscopy, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) equipped by EDS. All phases present in the above condition were described. The effects of solution annealing heat treatment temperature on the microstructure, te...

In this study, the grindability of cast magnetic alloys (Fe-Pt-Nb magnetic alloy and magnetic stainless steel) was evaluated and compared with that of conventional dental casting alloys (Ag-Pd-Au alloy, Type 4 gold alloy, and cobalt-chromium alloy). Grindability was evaluated in terms of grinding rate (i.e., volume of metal removed per minute) and grinding ratio (i.e., volume ratio of metal rem...

The relation between microstructure and creep property of austenitic heat-resistant cast steels with without Nb addition under the condition repeated vacuum carburizing quenching was investigated. Cr-carbide scale is formed on sample surface by a reaction, resulting in depletion Cr matrix adjacent to scale. A carburized layer consisting various fine carbides observed below Cr-depleted layer, de...

Steel containing 0.03% carbon, 1.35% copper and 0.84% nickel had yield strength in the 540-625 MPa (78-90 Ksi) range depending on thickness, ultimate tensile strength in the 625-690 MPa (90100 Ksi) range, and 25-30% elongation when air cooled after hot rolling. No brittle heat-affected zone was formed during manual or automatic submerged arc welding without pre-heating or postheating. The fract...