In this work, a Co-Fe-Ni catalyst was prepared and the effect of a range of operational variables such as gas hourly space velocity (GHSV), calcination temperature, calcination time and agent on its catalytic performance for green-fuels production was investigated. By application of different characterization techniques such as XRD, BET, TGA/DSC, and SEM, it was found that these parameters have...

The adsorption performance of Fe/ZSM-5 catalyst has been investigated in the SCR of NOx with propylene as the reducing agent. Freudlich equation was found to fit the adsorption isotherm satisfactorily if the system dispersion is considered. Fe/ZSM-5 catalyst showed reasonable NO adsorption capacity. The study on the influence of reaction temperature, gas space velocity and gas composition on th...

hydrogen was produced by steam reforming of dimethyl ether (dme) using a physical mixture of commercial hzsm-5 zeolite (for dme hydrolyzing) and cu/zno/al2o3 (for methanol steam reforming) as a catalyst in a fixed bed reactor. the experiments were performed at atmospheric pressure and in a temperature range from 270 to 310 °c. the effects of feed temperature and gas hourly space velocity (ghsv)...

Ordered mesoporous MnCo2O4 nanomaterials were successfully prepared through the nanocasting route using SBA-15 and KIT-6 as hard templates. These mesoporous nanomaterials were characterized using XRD, BET, TEM, NH3-TPD, H2-TPR, NO-TPD, XPS and DRIFT. The low temperature selective catalytic reduction (SCR) activity of NO with NH3 was investigated, which revealed that 3D-MnCo2O4 using KIT-6 as a ...

The activity of different transitional metals over modified H-ZSM-5 catalysts for methane conversion to aromatics was compared. The first group of catalysts was Mo-impregnated H-ZSM-5 zeolites with 1, 3 and 6 wt% of Mo. The second group was M(3 wt%)- impregnated H-ZSM-5 (M: Ag, Cd, Cr, Mo, Zn and Mn). The catalytic activity of the first group was investigated at 600, 700 and 800 °C and gas hour...

Cu–Zn/γ–Al2O3 catalysts were prepared by the impregnation method. Catalytic activity was evaluated for N2O decomposition in a fixed bed reactor. The fresh and used catalysts were characterized by several techniques such as BET surface area, X-ray diffraction (XRD), and scanning electron microscopy (SEM). The Cu–Zn/γ–Al2O3 catalysts exhibit high activity and stability for N2O decomposition in mi...

Cu/ZnO/Al2O3 catalyst with the addition of tri-promoters (Mn/Nb/Zr) was investigated respect to their catalytic activity and stability in a prolonged reaction duration methanol synthesis. Spent catalysts were characterized using N2 adsorption-desorption, FESEM/EDX, TEM, N2O chemisorption, XPS for physicochemical properties. The longevity study evaluated at two days, seven 14 days 300 °C, 31.25 ...

TiO2 supports doped with different amounts of Si were prepared by a sol-gel method, and 1 wt% vanadia (V2O5) loaded on Si-doped TiO2 was obtained by an impregnation method. The mole ratio of Si/Ti was 0.2, NOx conversion exceeds 94% at 300 degrees C and GHSV of 41,324 hr(-1), which is about 20% higher than pure V2O5/TiO2. The catalysts were characterized by XRD, BET, TEM, FT-IR, NH3-TPD, XPS, H...

We have reported previously the excellent performance of Fe-exchanged ZSM-5 for selective catalytic reduction (SCR) of NO with ammonia at high temperatures (300–400 C). In this work, we found that the reaction temperature could be decreased to 200– 300 C when a small amount of noble metal (Pt, Rh, or Pd) was added to the Fe-ZSM-5. The SCR activity follows the order Pt/FeZSM-5 > Rh/Fe-ZSM-5 > Pd...