In this study, nanocrystalline cellulose (NCC) was used for increasing the bonding strength of urea-formaldehyde (UF) resin adhesive, with a reduction of formaldehyde (HCHO) emissions. The surface of NCC was modified by 3-aminpropyltriethoxysilane (APTES) and 3-methacryloxypropyltrimethoxysilane (MPS) for the lack of compatibility with UF resin adhesive. The modified NCC was characterized by X-...

Urea-formaldehyde resins modified by melamine were synthesized by four catalysts (H2SO4, HCl, H3PO4, and NaOH/NH4OH) with a F/U/M molar ratio of 1.38/1/0.074. Resin structure and thermal behavior were studied by C-NMR and DSC techniques. For H2SO4, HCl, and H3PO4 catalysts, resins were prepared by two stage pH adjustment: the first pH stage was set at 1.25 (H3PO4 pH 1.60) and second pH stage wa...

A powdery product was obtained by the reaction of methylolated melamine with alkyl resorcinols to form melamine-bridged alkyl resorcinols (MARs). The effects of the addition of this powder on the bonding strength and formaldehyde emission of urea–formaldehyde (UF) resins were investigated. Three types of UF resins with a formaldehyde/urea molar ratio of 1.3 synthesized by condensation at pH 1.0...

ABSTRAKPanel kayu merupakan produk yang terbuat dari bahan direkatkan dengan menggunakan resin, perekat digunakan dalam produksi lapis resin urea-formaldehid (UF). Resin UF adalah thermosetting urea dan formaldehid akan mengeras jika dipanaskan dapat dicetak ulang. Pada penelitian ini, pembuatan baku Urea Formaldehyde Concentrate (UFC). Tujuan ini mempelajari pengaruh perubahan sifat kinerja UF...

a chelating resin is prepared by condensation polymerization of aniline with formaldehyde andcharacterized by ft-ir, elemental analysis and studied for the preconcentration and determination of traceplatinum ion from environmental water sample using inductively coupled plasma-atomic emission spectroscopy(icp-aes). the optimum ph value for sorption of the metal ions was 5. the maximum adsorption...

a chelating resin is prepared by condensation polymerization of aniline with formaldehyde andcharacterized by ft-ir, elemental analysis and studied for the preconcentration and determination of traceplatinum ion from environmental water sample using inductively coupled plasma-atomic emission spectroscopy(icp-aes). the optimum ph value for sorption of the metal ions was 5. the maximum adsorption...

A previous study of synthesizing low mole ratio urea–formaldehyde (UF) and urea–melamine–formaldehyde (UMF) resins, which included an acidic reaction step at the beginning of the typical resin synthesis procedure to obtain higher uron-type methylene–ether group contents, was repeated with the acidic reaction step extended to a higher viscosity. Compared to previous resins, the synthesized resin...

Low mole ratio urea-melamine-formaldehyde (UMF) resins synthesized with 2.5% and 5.0% melamine levels added at the beginning, middle, and end points of the first alkaline step of the typical urea-formaldehyde (UF) resin synthesis procedure were compared with typical UMF resins synthesized with melamine additions made at the final alkaline step. Various resin analysis, particleboard preparation,...

Several techniques have been used for sand production control in sandstone reservoirs.The main objective of this research is to present a suitable resin to be used as a consolidation agent in oil reservoirs. To achieve this purpose, urea-formaldehyde resin, phenol-formaldehyde resin, and modified urea-formaldehyde resin were selected to be studied. Core samples were made by the sand sample prov...

Novel melamine based free formaldehyde resin using glutaraldehyde as a condensing agent rather than formaldehyde has been synthesized under optimum conditions for use as a retanning agent. Characteristics and effects of the polymer as a retanning agent have been investigated against conventional melamine formaldehyde resin. Tear strength, tensile strength, elongation at break, and scanning elec...