An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...

Fatigue crack growth rate depends not only on the load amplitude, but also on the morphology of crack path. The strain energy density theory has the ability to analyze crack growth rate. A strain energy density crack growth model is proposed. It can predict the lifetime of fatigue crack growth for mixed mode cracks while an equation for mode I crack is also obtained. The validity of the model i...

Fatigue crack growth behavior of AZ61 magnesium alloy was investigated in low humidity (55% relative humidity) and 3.5% NaCl spray environments under various stress ratios. Fatigue crack growth rates became higher with increasing load ratio for both environments. However, the results of fatigue crack growth test under 3.5% NaCl spray environment showed lower fatigue crack propagation rate compa...

In this paper, the fatigue and fracture properties of bovine dentin are evaluated using in vitro experimental analyses. Double cantilever beam (DCB) specimens were prepared from bovine maxillary molars and subjected to zeroto-tension cyclic loads. The fatigue crack growth rate was evaluated as a function of the dentin tubule orientation using the Paris law. Wedge-loaded DCB specimens were also ...

Uniform drying causes a quasi-two-dimensional cellular crack pattern in a thin layer of paste. In our previous research, we found that such cracks are created in a capillary state, and that the growth speed is determined by the rate of increase in tension in the layer, rather than by the magnitude of the tension itself. In this paper, we present a theoretical investigation of the effects of inc...

Fatigue crack growth is examined in P/M 2124 aluminum alloys reinforced with SiC particles (SiCp) and whiskers (SiCw) over a wide spectrum of growth rates from 10 to 10 m per cycle. Effects of aging treatment, orientation of crack growth direction with respect to the rolling direction, mean stress (or stress ratio), and reinforcement volume percent on the fatigue crack growth threshold are inve...

DC electric potential technique has been used to monitor crack growth in conductive materials. A constant DC current is passed through these materials and the crack length is measured through the changes in the electrical voltage at the crack mouth. However, this method is not applicable in crack growth measurement in nonconductive materials or adhesively bonded joints. For these materials, a n...