The idea of smart corrosion inhibition is basis on either inhibitor consumption where it is needed or reducing harmful matrix interaction with it. In addition, applying corrosion inhibitor in a coating causes many problems such as loss of inhibition capability, coating degradation, or both. A useful technique to overcome this problem is applying of inert host systems of nanometer dimensions as ...

Corrosion inhibition of mild steel in 1 M HCl and 0.5 M H2SO4 by dapsone were studied by polarization resistance, Tafel polarization, electrochemical impedance spectroscopy (EIS) and weight loss measurement. Results obtained revealed that inhibition occurs through adsorption of the drug on metal surface without modifying the mechanism of corrosion process. Potentiodynamic polarization suggested...

In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of ...

Corrosion of complex electronic equipment is an increasingly serious problem, causing expensive damage. Corrosion occurs through out the entire life cycle during different stages of manufacturing, assembly, transport and storage of components and assemblies and during field operations of the equipment. Presence of moisture, chloride, sulphur dioxide, hydrogen sulphide and other airborne corrosi...

The wind turbine foundation serves as a permanent construction in the harsh marine corrosive environment, its anticorrosion design is essential to the safe use of the wind turbine structure. At present, there is a significant controversy over the local corrosion mechanism (such as pitting corrosion, and crevice corrosion) and its diffusion mechanism in the academic circle. In the paper, the Far...

The heterogeneous structure of Al alloys renders them susceptible to localized corrosion due to the different electrochemical properties existing in the Al-rich solid solution matrix and secondary phase particles. The galvanic interactions between these two phases can result in pit formation either through dissolution of the particles or corrosion of the matrix adjacent to the particles. This d...

Sour gas wells frequently co-produce elemental sulfur which can cause catastrophic corrosion of mild steel. As producing wells become increasingly sour, the incidence of sulfur corrosion will likely increase. Despite the severity of this problem, limited mechanistic information about this process exists in the literature. The objective of this study is investigation of the corrosion mechanism i...

BACKGROUND Previous studies regarding modular head-neck taper corrosion were largely based on cobalt chrome (CoCr) alloy femoral heads. Less is known about head-neck taper corrosion with ceramic femoral heads. QUESTIONS/PURPOSES We asked (1) whether ceramic heads resulted in less taper corrosion than CoCr heads; (2) what device and patient factors influence taper fretting corrosion; and (3) w...

This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu₂O film increased gradually. Its corrosion product was Cu₂(O...